| 1 | Effect of Nb,Mo and Ti on the Microstructures and Mechanical Properties of 700MPa Weathering Steel显示文摘Using metallurgical structure observation and measurement of mechanical properties such as micro-hardness,tensile test,cold-bend,the effect of Nb,Mo and Ti on the structure and mechanical properties of 700MPa weathering steel was studied under the same rolling conditions.The results show the formation of M/A is promoted by Mo,while inhibited by Ti.Furthermore,M/A island,as a hard phase,is harm to the material toughness and plasticity;high M/A island fraction will result in obvious crack during cold bending.The effect of Nb on increasing the strength of experiment steel is very important.The Nb content of 700MPa steel must be higher than 0.05% to ensure the strength.The optimal mechanical properties of the experiment steel will be gained by the proper match ratio of Nb,Mo and Ti.The industry trial production of 700MPa high-strength weathering steel for container was also developed. | WANG Bing 1,SONG Yu-lai 2,WEN Xiao-ming 3,WANG Hou-xin 4,LIU Qing-you 1 (1.Institute for Structural Materials of CISRI,Beijing 100081,China 2.Research and Development Center of Wuhan Iron and Steel (Group) Corp.,Wuhan 430080,Hubei,China 3.Benxi Iron and Steel Group Limited Company Benxi 117000,Liaoning,China 4.CITIC-CBMM Microalloying Technology Center,Beijing 100081,China) | 2011 | Journal of Iron and Steel Research(International)2011，18，S1： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员