In-situ SEM observation on fracture behavior of austempered silicon alloyed steel

查看全文 作　　者：Vuorinen [1]Esa;Grahn [1]Jonny

机构地区：[1]Division of Engineering Materials,Department of Applied Physics and Mechanical Engineering,Lule University of Technology

出　　处：《China Foundry》索引2009年第6卷第3期,共6页

基　　金：supported by Swedish Institute of Sweden (No. 200/01954/2007/China Bilateral programme) 摘　　要：Crack initiation, propagation and microfracture processes of austempered high silicon cast steel have been investigated by using an in-situ tensile stage installed inside a scanning electron microscope chamber. It is revealed that micro cracks always nucleate at the yielding near imperfections and the boundary of matrix-inclusions due to the stress concentration. There are four types of crack propagations in the matrix: crack propagates along the boundary of two clusters of bainitic ferrite; crack propagates along the boundary of ferrite-austenite in bainitic ferrite laths; crack propagates into bainitic ferrite laths; crack nucleates and propagates in the high carbon brittle plate shape martensite which is transformed from some blocky retained austenite due to plastic deformation. Based on the observation and analysis of microfracture processes, a schematic diagram of the crack nucleation and propagation process of high silicon cast steel is proposed. 关键词：high SILICON cast STEEL bainitic FERRITE AUSTEMPERING in-situ SEM OBSERVATION fracture

相关文献

参考文献（11）
引证文献（2）
耦合文献（1）

参考文献(11)

引证文献(2)

耦合文献(1)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

In-situ SEM observation on fracture behavior of austempered silicon alloyed steel

参考文献(11)

引证文献(2)

耦合文献(1)

用户提示