Microstructure and sliding wear behavior of pseudo-alloy PS45/CuAl8 composite coating sprayed by HVAA technique

查看全文 作　　者：WU Yaosha a , ZENG Dechang a , LIU Zhongwu a , QIU Wanqi a , YU Hongya a , ZHONG Xichun a , LI Shangzhou a , and MA Yuexin b a School of Materials Science & Engineering, South China University of Technology, Guangzhou 510640, China b Optoelectronic Engineering Department, Zhongshan Torch Polytechnic, Zhongshan 528436, China

出　　处：《Rare Metals》索引2012年第31卷第2期,共5页

基　　金：supported by Key Projects of the Guang-dong Provincial Science & Technology Program (Nos.2009A090100045 and 2010A090200077);Project of the Zhongshan Civic Science & Technology Program (No.20103A262) 摘　　要：A pseudo-alloy PS45/CuAl8 composite coating was sprayed on steel substrate by high-velocity activated arc spraying (HVAA) process. Its sliding wear behavior at room temperature was evaluated by M-2000 wear tester. For comparison, a single CuAl8 coating was also prepared and tested under the same conditions. It is found that the pseudo-alloy composite coating consists of α-Cu and γ-Ni metallic matrix phases together with homogenously distributed minor Al 2 O 3 , Cr 2 O 3 oxide phases. Moreover, pseudo-alloy coating possesses much better sliding wear resistance than CuAl8 coating due to the enhanced hardness and microstructural homogenization. Fatigue wear and abrasive wear are responsible for the wear-down mechanism of the pseudo-alloy coating. 关键词：surface science HVAA pseudo-alloy composite coating PS45/CuAl8 sliding wear MICROSTRUCTURE

相关文献

参考文献（19）
引证文献（0）
耦合文献（6）

参考文献(19)

耦合文献(6)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Microstructure and sliding wear behavior of pseudo-alloy PS45/CuAl8 composite coating sprayed by HVAA technique

参考文献(19)

耦合文献(6)

用户提示