EFFECT OF ANNEALING ON DAMPING CAPACITIES OF AS-CAST ZA27 ALLOY

查看全文 作　　者：Z.M. [1]Zhang;J. C. [2]Wang;H.Z. [1]Liu;X.F. [1]Guo

机构地区：[1]School of Materials Science & Engineering, Xi'an University of Technology,Xi'an 710048, China;[2]State Key Laboratory of Solidification Processing, Northwestern PolytechnicalUniversity, Xi'an 710072, China

出　　处：《Acta Metallurgica Sinica(English Letters)》索引2006年第19卷第5期,共6页

基　　金：This work was supported by the National Natural Science Foundation of China(No.50075068);Scientific Research Project of Department of Education of Shaanxi Province(No.03JK132);Natural Science Foundation of Shaanxi Province(No.2003E1 11). 摘　　要：ZA27 alloy was prepared by casting with permanent mold and then annealed at 250℃ for 1-4h. The damping capacity of the alloy was measured using a testing apparatus based on the cantilever beam technique. It was found that the as-cast ZA27 alloy possesses high damping capacity with the value of 1.3 × 10-3 at 320Hz. After annealed at 250℃ for 1h, the damping capacity decreases to 1.1 × 10-3 and then remains constant even when the annealing time is increased to 4h. The microstructure of the as-cast ZA27 alloy consists of large dendrites of Al-rich primary (?)-phases, eutectoid (?) and nonequilibrium eutectic phases (?). After annealing at 250℃ for 1h, the (?)phase disappears due to dissolution into the matrix, and the spacing between the flakes of eutectoid increases. The further increase in the annealing time has little effect on the spacing. The damping mechanism of the alloy was discussed considering the thermoelastic damping and defect damping. The value of thermoelastic damping accounts only for 7%-8% in the overall damping in cantilever beam damping measurements and the damping capacity of the ZA27 alloy came mainly from defect damping. 关键词：ZA27合金退火阻尼容量铸造合金

相关文献

参考文献（2）
引证文献（3）
耦合文献（0）

参考文献(2)

引证文献(3)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

EFFECT OF ANNEALING ON DAMPING CAPACITIES OF AS-CAST ZA27 ALLOY

参考文献(2)

引证文献(3)

用户提示