Densification behavior of high Nb containing TiAl alloys through reactive hot pressing

查看全文 作　　者：Yanhang [1]Wang;Junpin [1]Lin;Yuehui [2]He;Yanli [1]Wang;Guoliang [1]Chen

机构地区：[1]State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China;[2]State Key Laboratory for Powder Metallurgy, Central South University, Changsha 410083, China

出　　处：《Journal of University of Science and Technology Beijing》索引2007年第14卷第3期,共5页

基　　金：the Key Grant Project of the Ministry of Education of China (No.704008);the program fromNew Century Excellent Talents in University (No.NCET-04-01017). 摘　　要：Densification behavior of high Nb containing TiAl alloys through reactive hot pressing was investigated. The results showed that the density of the sample hot pressed at 1400°C could reach a near full density of 98.37%. However, the densification abnormality was observed at 1500°C. The diffusion of elemental Nb during microstructural evolution is an important aspect affecting densification, which will form pore nests. With the increase of hot pressing temperature, the diffusion of Nb becomes more adequate. HIP (Hot isostatic pressing) treatment can only decrease porosity to some extent, but cannot eliminate it completely. 关键词：热压高铌钛铝合金致密化粉末冶金

相关文献

参考文献（2）
引证文献（0）
耦合文献（3）

参考文献(2)

耦合文献(3)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Densification behavior of high Nb containing TiAl alloys through reactive hot pressing

参考文献(2)

耦合文献(3)

用户提示