Preparation and characterization of three-dimen-sionally ordered macroporous polystyrene via atom-transfer radical polymerization

查看全文 作　　者：ZHANG [1]Xu;YAN [1]WeiDong;YANG [1]HuiFang;WANG [2]BaiQuan

机构地区：[1]Institute of Polymer Science and Engineering, Hebei University of Technology, Tianjin 300130, China;[2]State Key Laboratory of Elemento-organic Chemistry, Nankai University, Tianjin 300071, China

出　　处：《Chinese Science Bulletin》索引2008年第53卷第24期,共5页

基　　金：Supported by National Natural Science Foundation of China (Grant No. 50273009);Natural Science Foundation of Hebei Province (Grant No. E2007000052);Science Research Plan of Department of Education,Hebei Province (Grant No. 2007307);Doctor Open Foundation of Key Laboratory of Functional Polymer Material of Ministry of Education,Nankai University) (Grant No. 2006-007) 摘　　要：Three-dimensionally ordered macroporous polystyrene(3DOM PS) with pore size of 350 nm was fabricated using Cp2Co/Ethyl 2-bromoisobutyrate(EBiB) catalytic system by ATRP.The resulting polymers were detected by FT-IR,1H-NMR,SEM,and GPC.The microstructure of 3DOM PS was confirmed by FT-IR and 1H-NMR.SEM micrographs show that both silica spheres within the templates and pores in the 3DOM polystyrene are arranged in highly ordered fashion,and the shrinkage of the pores in the 3DOM PS is 24%.GPC curves show that the 3DOM PS possesses slightly lower Mn and narrow MWD compared with bulk one.This result indicats that living polymerization is different from non-living polymerizationin in the confined space. 关键词：有序大孔聚合物聚苯乙烯原子传输聚合作用

相关文献

参考文献（10）
引证文献（3）
耦合文献（0）

参考文献(10)

引证文献(3)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Preparation and characterization of three-dimen-sionally ordered macroporous polystyrene via atom-transfer radical polymerization

参考文献(10)

引证文献(3)

用户提示