Effect of Withdrawal Rates on Microstructure and Creep Strength of a Single Crystal Superalloy Processed by LMC

查看全文 作　　者：Chengbao [1]Liu;Jian [1]Shen;Jian [2]Zhang;Langhong [1]Lou

机构地区：[1]Superalloys Division, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;[2]National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

出　　处：《Journal of Materials Science & Technology》索引2010年第26卷第4期,共5页

摘　　要：A nickel base single crystal (SC) superalloy was directionally solidified using liquid metal cooling (LMC) process at various withdrawal rates. The microstructure was refined as increasing the withdrawal rate from 3 to 12 mm/min. However, higher withdrawal rate of 15 mm/min induced the formation of stray grains. Size and volume fraction of the eutectics were found to decrease with the increasing in withdrawal rate. After solution heat treatment at 1250℃, un-dissolved eutectic was observed in specimens. High temperature creep rupture life was observed to be very sensitive to the fraction of these remaining eutectics. Creep rupture tests at 1000℃/235 MPa showed that refined microstructure and low fraction of the remaining eutectic lead to significant improvement of the rupture life. 关键词：单晶高温合金蠕变断裂寿命定向凝固高温合金加工强度组织戒断微观结构

相关文献

参考文献（23）
引证文献（20）
耦合文献（0）

参考文献(23)

引证文献(20)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effect of Withdrawal Rates on Microstructure and Creep Strength of a Single Crystal Superalloy Processed by LMC

参考文献(23)

引证文献(20)

用户提示