Thermal behaviors and growth of reduced ferronickel particles in carbon-laterite composites

查看全文 作　　者：HUANG [1,2]Donghua;ZHANG [1]Jianliang;MAO [1]Rui;CAO [1]Mingming 高影响力作者 机构地区：[1]School of Metallurgical and Ecological Engineen'ng, State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;[2]Journals Publishing Center, University of Science and Technology Beijing, Beijing 100083, China高影响力机构 出　　处：《Rare Metals》索引2011年第30卷第6期,共7页高影响力期刊 摘　　要：The thermal behaviors of single laterite ore and graphite-laterite mixtures were investigated by thermogravimetry (TG), derivative thermo-gravimetry (DTG), and differential thermal analysis (DTA). Four mass loss steps maximized at about 78, 272, 583, and 826°C are observed for the laterite ore, representing the vaporization of free water, the dehydroxylation of goethite, the decomposition of serpentines, and the second dehydroxylation of serpentines, respectively. The reduction reactions of the graphite-laterite mixtures start at around 700°C and can be divided into three major temperature regions. Coal-laterite composites with an addition of 10 wt.% CaO were roasted at 1100-1350°C for 30 min, and the reduced samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results indi-cate that the reduction reactions proceed more completely at higher temperatures. The growth of the reduced ferronickel particles is greatly influenced by the roasting temperature. Obvious growth of the reduced ferronickel particles appears with the formation of worm-like crystals for the sample reduced at 1250°C, and spheric particles are observed for the sample reduced at 1300°C. When the reduction temperature in-creases to 1350°C, the reduced ferronickel particles agglomerate to ferronickel granules of 3-8 mm in diameter. The main elements in the granules include iron, nickel, chromium, carbon, and sulfur, with the content of nickel and that of iron of 9.08 wt.% and 85.21 wt.%, respec-tively. 关 键 词：复合材料 红土矿 铁粒子 热行为 镍矿 扫描电子显微镜 焙烧温度 碳
相关文献

参考文献(18)

引证文献(2)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费