Quantitative analysis of work hardening and dynamic softening behaviors of Cu-6 wt pct Ag binary alloy based on true stress vs strain curves

查看全文 作　　者：Menghan [1]WANG;Wenhao [1]WANG;Jingjing [1]DONG;Linhui [1]ZHANG;Yunping [2]LI;Akihiko [2]CHIBA 高影响力作者 机构地区：[1]School of Material Science and Engineering, Chongqing University, Chongqing 400044, China;[2]Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan高影响力机构 出　　处：《Acta Metallurgica Sinica(English Letters)》索引2012年第25卷第6期,共15页高影响力期刊 基　　金：supported by the Chongqing Natural Science Foundation(No.CSTC2009BA4065) 摘　　要：The work hardening and dynamic softening behaviors of Cu-6 wt pct Ag binary alloy were studied by hot compression tests under temperature range of 700-850℃ at strain rates of 0.01-10s-1.The critical conditions for the onset of dynamic recrystallization (DRX) were determined based on the conventional strain hardening rate curves (dσ/dε versus σ).The progress of DRX was analyzed by constructing a model of volume fraction of DRX based on flow curves.The strain rate sensitivity (SRS) and activation volume V were calculated.The results show that the DRX almost can happen under all deformation conditions even at high Z deformations where dynamic recovery (DRV) is the main softening mechanism.The DRX fraction curves can well predict the DRX behavior.The strain has significant effects on SRS at the strain rates of 0.01s-1 and 10s-1 which are mainly due to off-equilibrium saturation of dislocation storage and annihilation while the effects of the temperature on the SRS are based on the uniformity of microstructure distribution.The formation of 'forest' of dislocation is contributed to the low activation volume V*(about 168b3) which is independent of Z values at the initial deformation.The cross-slip due to dislocation piled up beyond the grain boundaries or obstacles is related to the low activation volume under the high Z deformation conditions at high strain (ε=0.6) while the fine DRX grains coarsed is the main reason for the high activation volume at low Z under the same strain conditions. 关 键 词：应变曲线 动态软化 加工硬化 二元合金 行为 定量分析 重量 应变速率敏感性
相关文献

参考文献(38)

引证文献(1)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费