Dynamic Strain Aging in a Newly Developed Ni-Co-Base Superalloy with Low Stacking Fault Energy

查看全文 作　　者：Chenggang [1]Tian;Chuanyong [1]Cui;Ling [1]Xu;Yuefeng [1]Gu;Xiaofeng [1]Sun 机构地区：[1]Superalloys Division,Institute of Metal Research,Chinese Academy of Sciences 出　　处：《Journal of Materials Science & Technology》索引2013年第29卷第9期,共6页 基　　金：partly supported by 'Hundred of Talents Projects';the National Basic Research Program (973 Program) of China under grant No. 2010CB631206;the National Natural Science Foundation of China (NSFC) under Grant Nos. 51171179, 51128101 and 51271174 摘　　要：Characteristics of dynamic strain aging(DSA) in a Nie Co-base superalloy were studied by tensile tests at temperatures ranging from 250℃ to 550℃ and strain rates ranging from 3×10-5 to 8×10-4 s-1.Serrated flow in the tensile stress-strain curves was observed in the temperature range from 300℃ to 500℃.Normal DSA behavior was found at temperatures ranging from 300℃ to 350℃,while inverse DSA behavior was observed at temperatures ranging from 400℃ to 500℃.The yield strength,ultimate tensile strength,elongation,work hardening index,and fracture features were not affected by temperature and strain rates in DSA regime.Negative strain-rate sensitivity of flow stress was observed in DSA regime.The analysis suggests that the ordering of the substitutional solutes around some defects like mobile dislocations and stacking faults due to the thermal activated process may cause the serrations on the tensile curves. 关 键 词：动态应变时效 钴基高温合金 应变速率敏感性 层错能 温度范围 开发 极限拉伸强度 加工硬化指数