Preparation,thermal stability and biocompatibility studies of gelatin-induced hydroxyapatite co-substituted with essential physiological trace elements

查看全文 作　　者：Ming [1]Ma;Bing [1]Zhang;Weipeng [1]Lu;Junli [2]Liu;Yanchuan [1]Guo 高影响力作者 机构地区：[1]Key Laboratory of Photochemical Conversion and Optoelectronic Material, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences;[2]The 306th Hospital of People’s Liberation Army高影响力机构 出　　处：《Chinese Science Bulletin》索引2014年第59卷第7期,共10页高影响力期刊 基　　金：supported by Programs of Interna-tional Science and Technology Corporation,China(S2013ZR0442);Beijing Municipal Science and Technology Project(Z131100005213007) 摘　　要：Gelatin-induced hydroxyapatite with combined substitution of essential physiological trace elements(G-FAP)was prepared by a precipitation method.Pure hydroxyapatite(HAP)and ion-substituted hydroxyapatite(FAP)were also prepared for comparison.The characteristics of the precipitated powders were determined using X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),Fourier transform infrared spectroscopy(FT-IR),specific surface area measurement(SSA),X-ray fluorescence spectroscopy(XRF),and thermogravimetric(TG)analysis.The biocompatibility was also determined by an in vitro investigation with MC3T3-E1 cells.SEM and TEM results showed that the G-FAP powders were composed of dense aggregates of agglomerated whisker-like crystals of200–300 nm in length and 10–20 nm in width.XRD and FT-IR analyses indicated the formation of pure apatite phase,and the substituted ions and gelatin did not change the diffraction pattern of the precipitated powders.The SSAs of the precipitated powder were 64.741,72.492,and107.745 m2/g,for HAP,FAP,and G-FAP,respectively.XRF analysis showed that Na+,Mg2+,and F-were substituted into the crystal lattice.TG results showed a reduced thermal stability of the precipitated G-FAP powders,with an advanced phase transformation beginning at800°C and a serious phase transformation from hexagonal apatite phase to rhombohedral b-TCP phase at 1,200°C in comparison with HAP and FAP.In vitro biological tests showed non-cytotoxic effects for all powders.However,G-FAP stimulated the proliferation of MC3T3-E1 cells earlier than HAP and FAP.The present G-FAP will therefore be a promising primary biomaterial for bone regeneration,tooth filling,or as a coating for metal artificial limbs. 关 键 词：羟基磷灰石 微量元素 热稳定性 生物相容性 明胶 制备 诱导 生理
相关文献

参考文献(46)

引证文献(2)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费