Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy

查看全文 作　　者：[1,2]刘德学;CHENG [1,2]Xiaowei;ZHANG [1,2]Xiao;DING [1,2]Yutian 高影响力作者 机构地区：[1]School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China;[2]State Key Laboratory of Advanced Processing and Recyling of Nonferrous Metals, Lanzhou 730050, China高影响力机构 出　　处：《Journal of Wuhan University of Technology(Materials Science)》索引2016年第31卷第6期,共9页高影响力期刊 基　　金：Funded by the National Natural Science Foundation of China(Nos.51664041 and 51365029);the Gansu Science and Technology Support Program-industrial Category(No.1604GKCA038);the Fundamental Research Funds for the Universities in Gansu Province;the Program for Major Projects of Science and Technology in Gansu Province(No.145RTSA004) 摘　　要：The effects of the heating process and hot extrusion on the microstructure and properties of inconel 625 alloy were studied. The experimental results showed that the properties of Inconel 625 alloy could be improved through the heating process and hot extrusion concomitant with a reduced corrosion rate. The M23C6 carbide, generated in the heating process, was retained and distributed at the grain boundary during the process of hot extrusion, which had an important influence on both elongation and corrosion resistance. The improvement of the comprehensive properties of the material, as measured by a tensile test at room temperature, was correlated with the dissolution of segregation Nb. A typical ductile fracture changed to a cleavage fracture where secondary cracks could be clearly seen. With the increase of the extrusion ratio, the real extrusion temperature was higher, which led to more dissolution of the M23C6 carbide, decreased the number of secondary cracks, enhanced the effect of solid solution strengthening, and reduced the intergranular corrosion rate. Under the condition of a high extrusion ratio and a high extrusion speed, the less extrusion time made it possible to obtain organization with a smaller average grain size. Moreover, in this case, the M23C6 carbide and segregated Nb did not have enough time to diffuse. Thus all samples exhibited medium strengths and corrosion rates after extrusion. 关 键 词：INCONEL 组织性能 加热过程 挤压过程 合金 M23C6 挤出温度 腐蚀速率
相关文献

参考文献(29)

引证文献(5)

耦合文献(48)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费