Effects and mechanisms of fluorite on the co-reduction of blast furnace dust and seaside titanomagnetite

查看全文 作　　者：Tian-yang [1,2]Hu;Ti-chang [1,2]Sun;Jue [1,2]Kou;Chao [1,2]Geng;Yong-qiang [1,2]Zhao

机构地区：[1]School of Civil and Resources Engineering, University of Science and Technology Beijing, Beijing 100083, China;[2]Key Laboratory of Ministry of Education of China for Efficient Mining and Safety of Metal Mines, Beijing 100083, China

出　　处：《International Journal of Minerals,Metallurgy and Materials》索引2017年第24卷第11期,共10页

基　　金：financially supported by the National Natural Science Foundation of China (No. 51474018) 摘　　要：The co-reduction roasting and grinding-magnetic separation of seaside titanomagnetite and blast furnace dust was investigated with and without fluorite addition at a reduction roasting temperature of 1250°C for 60 min, a grinding fineness of-43 μm accounting for 69.02 wt% of the total, and a low-intensity magnetic field strength of 151 kA/m. The mineral composition, microstructure, and state of the roasted products were analyzed, and the concentrations of CO and CO_2 were analyzed in the co-reduction roasting. Better results were achieved with a small fluorite dosage(≤4 wt%) in the process of co-reduction. In addition, F^- was found to reduce the melting point and viscosity of the slag phase because of the high content of aluminate and silicate minerals in the blast furnace dust. The low moisture content of the blast furnace dust and calcic minerals inhibited the hydrolysis of CaF_2 and the loss of F^-. Compared with the blast furnace dust from Chengdeng, the blast furnace dusts from Jiugang and Jinxin inhibited the diffusion of F-when used as reducing agents, leading to weaker effects of fluorite. 关键词：seaside TITANOMAGNETITE blast FURNACE dust co-reduction ROASTING FLUORITE MECHANISMS

相关文献

参考文献（24）
引证文献（7）
耦合文献（54）

参考文献(24)

引证文献(7)

耦合文献(54)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effects and mechanisms of fluorite on the co-reduction of blast furnace dust and seaside titanomagnetite

参考文献(24)

引证文献(7)

耦合文献(54)

用户提示