Effect of Oxidizing Atmosphere on the Surface of Titanium Dental Implant Material

查看全文 作　　者：Mohammad [1]Khodaei;Akram [2]Alizadeh;Hamid Reza Madaah [3]Hosseini 高影响力作者 机构地区：[1]Department of Materials Science and Engineering,Golpayegan University of Technology,Golpayegan 87717-65651,Iran;[2]Department of Tissue Engineering,School of Advanced Technologies,Shahrekord University of Medical Sciences,Shahrekord 88157-13471,Iran;[3]Department of Materials Science and Engineering,Sharif University of Technology,Tehran 14588-89694,Iran高影响力机构 出　　处：《Journal of Bionic Engineering》索引2019年第16卷第6期,共9页高影响力期刊 摘　　要：Direct oxidation is a simple and effective method for titanium surface treatment.In this research,a titanium sample was directly oxidized at the high temperature in two different atmospheres,air and pure oxygen,to obtain better atmosphere for titanium surface treatment.The results of the Raman spectroscopy indicated that in both atmospheres,the rutile bioactive phase(TiO2)has been formed on the titanium surface.The results of X-ray diffraction(XRD)also revealed that the surface of oxygen-treated sample was composed of the rutile phase and titanium monoxide(TiO),while at the surface of the air-treated sample,the rutile phase and titanium dioxide had been formed.Further,the results of Field Emission Scanning Electron Microscopy(FE-SEM)showed that by the surface treatment of titanium in both atmospheres,some micro-features including cracks thinner than 30 nm were formed on the surface.Because of more apatite forming ability and fewer water contact angle and more L-929 cell attachment of the air-treated titanium,it seemed that air,in comparison to the pure oxygen,is more promising atmosphere for the direct oxidation of titanium and improving its biofunctionalization. 关 键 词：titanium implant surface treatment direct oxidation ANATASE RUTILE biomedical-materials
相关文献

参考文献(27)

引证文献(1)

耦合文献(16)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费