Friction of metal-matrix self-lubricating composites: Relationships among lubricant content, lubricating film coverage, and friction coefficient

查看全文 作　　者：Jinkun [1,2]XIAO;Yuqing [1]WU;Wei [1]ZHANG;Juan [3]CHEN;Chao [1]ZHANG 高影响力作者 机构地区：[1]College of Mechanical Engineering,Yangzhou Universiy,Yangzhou 225127,China;[2]College of Chemistry and Chemical Engineering,Yangzhou University,Yangzhou 225002,China;[3]Testing Center,Yangzhou University,Yangzhou 225009,China高影响力机构 出　　处：《Friction》索引2020年第8卷第3期,共14页高影响力期刊 基　　金：The authors would like to thank the National Natural Science Foundation of China(Grant No.51804272);Natural Science Foundation of Jiangsu Province(Grant No.BK20160472);Natural Science Foundation of the Jiangsu Higher Education Institutions of China(Grant No.17KJB460017);Project funded by China Postdoctoral Science Foundation(Grant No.2018M640526);Jiangsu Planned Projects for Postdoctoral Research Funds(Grant No.1601095C and 2018K073C);Postgraduate Research&Practice Innovation Program of Jiangsu Province(Grant No.SJCX17—0623);Marine Science and Technology Project of Jiangsu Province(Grant No.HY2017-10);Cooperation Funding of Yangzhou City-Yangzhou University(Grant No.YZU201722);Jiangdu Advanced Equipment Engineering Institute of Yangzhou University(Grant No.2017-01)for the financial support provided. 摘　　要：Metal-matrix self-lubricating composites can exhibit excellent tribological properties owing to the release of solid lubricant from the matrix and the formation of a lubricating film on the tribosurface.The coverage of the lubricating film on a worn surface significantly influences the sliding process.However,it is difficult to quantify the film coverage owing to the thin and discontinuous character of the lubricating film and the high roughness of the worn surface.A quantitative characterization of the lubricating film coverage based on X-ray photoelectron spectroscopy(XPS)analysis was developed in this study.The friction tests of Cu-MoS2 composites with a MoS2 content of 0-40 vol%were conducted,and the worn surfaces of the composites were observed and analyzed.Further,the influence of the MoS2 volume content on the coverage of the lubricating film on the worn surface was investigated.The relationships among the volume fraction of the lubricant,coverage of the lubricating film,and the friction coefficient were established.The friction model for the metal matrix self-lubricating composites was developed and verified to facilitate the composition design and friction coefficient prediction of self-lubricating composites. 关 键 词：self-lubricating composites friction coefficient lubricating film XPS
相关文献

参考文献(38)

引证文献(8)

耦合文献(33)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费