Effect of processing parameters on the densification of an additively manufactured 2024 Al alloy

查看全文 作　　者：Qiyang [1]Tan;Yingang [1]Liu;Zhiqi [1]Fan;Jingqi [1]Zhang;Yu [1]Yin;Ming-Xing [1]Zhang

机构地区：[1]School of Mechanical and Mining Engineering,The University of Queensland,St.Lucia,QLD 4072,Australia

出　　处：《Journal of Materials Science & Technology》索引2020年第58卷第23期,共12页

基　　金：ARC Discovery Project for funding support (No. DP180102454)。 摘　　要：Understanding the densification behaviours and formation mechanisms of defects are essential to fabricate high quality and high strength aluminium components using selective laser melting(SLM) technology. In this work, the effects of laser power and scanning speed on the densification, defects evolution and their formation mechanisms in a SLMed 2024 aluminium(Al) alloy were investigated in consideration of the corresponding laser energy input, melting mode transition and microstructural evolution. The results showed that optimizing the processing parameters effectively reduced the porosity level below1% by avoiding the lack of fusion and keyhole melting mode, and minimizing the gas pores. However,optimization of the processing parameters could not eliminate the columnar structure associated with the SLMed 2024 Al alloy, which contributed to the hot-tearing cracks in the SLMed parts. It was found that the dependence of porosity formation on SLM processing parameters was contrary to the crack density. Hence, to further improve the SLM-processability of the 2024 Al alloy it is necessary to develop SLM methods in order avoid the hot-cracking within the optimized processing parameter window associated with the minimum porosity formation. 关键词：Powder Bed Fusion Aluminum alloys METALLOGRAPHY DEFECTS SEM

相关文献

参考文献（73）
引证文献（28）
耦合文献（0）

参考文献(73)

引证文献(28)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effect of processing parameters on the densification of an additively manufactured 2024 Al alloy

参考文献(73)

引证文献(28)

用户提示