Microhardness,microstructure and electrical properties of ZVM ceramics

查看全文 作　　者：Abdel-Mageed [1]H.KHAFAGY;Sanaa M.EL-[2]RABAIE;Mohamed [2]T.DAWOUD;[1]M.T.ATTIAb

机构地区：[1]Physics Department,Faculty of Science,Menufiya University,Shebin El-Koom 32511,Egypt;[2]Physics and Engineering Mathematics Department,Faculty of Electronic Engineering,Menufiya University,Menouf 32952,Egypt

出　　处：《Journal of Advanced Ceramics》索引2014年第3卷第4期,共10页

摘　　要：The effect of Mn_(3)O_(4)addition on microhardness,microstructure and electrical properties of vanadium oxide doped zinc oxide varistor ceramics is systematically investigated.The Vicker’s microhardness HV has decreased with increasing the amount of Mn3O4.Also,the average grain size has decreased from 27.51μm to 19.55μm with increasing the amount of Mn_(3)O_(4) up to 0.50 mol%,whereas an increase in Mn_(3)O_(4) up to 0.75 mol%has caused the average grain size to increase and then it decreases with increasing Mn_(3)O_(4)from 0.75 mol%to 1.00 mol%.The sintered density has decreased from 5.38 g/cm3 to 5.31 g/cm3 with increasing the amount of Mn_(3)O_(4).The varistor ceramic modified with 0.50 mol%Mn_(3)O_(4) has exhibited excellent nonlinear properties,with 16.29 for the nonlinear coefficient and 441.9μA/cm2 for the leakage current density.Furthermore,the sample doped with 0.50 mol%Mn_(3)O_(4) has been found to possess donor density as 0.77×10^(18) cm^(-3) and 0.916 eV barrier height. 关键词：CERAMICS electrical properties MICROSTRUCTURE VARISTOR Mn3O4 doped ZnO-V2O5 varistor

相关文献

参考文献（35）
引证文献（2）
耦合文献（14）

参考文献(35)

引证文献(2)

耦合文献(14)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Microhardness,microstructure and electrical properties of ZVM ceramics

参考文献(35)

引证文献(2)

耦合文献(14)

用户提示