Simultaneously realizing good volumetric entropy change and mechanical strength of La_(0.8)Ce_(0.2)Fe_(11.51)Mn_(0.19)Si_(1.3)H_(y) plates

查看全文 作　　者：Juan [1,2]Cheng;Caiyin [1]You;Bo [2]Li;Yaru [2]Guo;Zhaojie [2]Li;Lei [2]Gao;Pengyu [2]Wang 高影响力作者 机构地区：[1]School of Materials Science and Technology,Xi'an University of Technology,Xi'an,710048,China;[2]State Key Laboratory of Baiyunobo Rare Earth Resource Researches and Comprehensive Utilization,Baotou Research Institute of Rare Earths,Baotou,014030,China高影响力机构 出　　处：《Journal of Rare Earths》索引2023年第41卷第10期,共7页高影响力期刊 基　　金：the ISF-SFC Joint Research Program(51961145305(NSFC));the National Natural Science Foundation of China(5217119);the Key Research and Development Program of Shanxi Province(2021KWZ-12);the IMAR(Inner Mongolia Autonomous Region)Natural Science Foundation(2021MS05016);the Northern Rare Earth Project(BFXT-2021-D-0013)。 摘　　要：It is hard to get a high-strength La(Fe,Si)_(13)-based hydrides owing to the brittle feature of hydrides.In this work,we fabricated the La_(0.8)Ce_(0.2)Fe_(11.51)Mn_(0.19)Si_(1.3)plates through hot pressing at 1323 K for various time.Subsequently,the saturated hydrogenization is achieved at 593 K in H_2 atmosphere of 0.13 MPa for 210 min.The microstructure and magnetocaloric properties were investigated by an X-ray diffractometer,a scanning electron microscope and the Versa-Lab.Under magnetic fields of 0-2 T,the maximal volumetric entropy change is 91.4 mJ/(cm^(3)·K)at 297 K for the hydride plates.The hydride plate simultaneously has excellent mechanical properties with the maximum bending strength of 213 MPa,which suggest that the hot pressing followed by hydrogenation could be an effective route of fabricating La(Fe,Si)_(13)-based hydrides for the potential application in the magnetic refrigerator. 关 键 词：Magnetocaloric effect Mechanical strength Volumetric entropy change HOT-PRESSING Rare earths
相关文献

参考文献(33)

引证文献(1)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费