Effects of Alloying Elements on Microstructure and Erosion Resistance of Fe-C-Cr Weld Surfacing Layer

查看全文 作　　者：Daqian SUN, Wenquan WANG, Zhaozhi XUAN, Yue XU and Zhenfeng ZHOUSchool of Materials Science and Engineering, Jilin University, Changchun 130025, China

出　　处：《Journal of Materials Science & Technology》索引2003年第19卷第4期,共4页

摘　　要：Effects of alloying elements on microstructure and erosion resistance of Fe-C-Cr weld surfacing layer have been studied. The experimental results show that increasing C and Cr content favors improving the erosion resistance of the layer, and the excessive C and Cr result in decreasing the erosion resistance at 90 deg. erosion. That Mo, Nb or Ti improves the erosion resistance of Fe-C-Cr weld surfacing layer is mainly attributed to increasing the amount of M7C3 and forming fine NbC or TiC in austenite matrix, but the excessive Mo, Nb or Ti is unfavorable. The addition of Mo, Nb and Ti in proper combination possesses stronger effect on improving the erosion resistance and the erosion resistance (εA) of Fe-C-Cr weld surfacing layer with fine NbC, TiC and M7C3 distributing uniformly in austenite matrix obviously increases to 2.81 at 15 deg. erosion and 2.88 at 90 deg. erosion when the layer composition is 3.05C, 20.58Cr, 1.88Mo, 2.00Nb and 1.05Ti (in wt pct). 关键词：合金元素抗腐蚀性焊接表面层微观结构铁碳铬合金 Fe-C-Cr合金

相关文献

参考文献（6）
引证文献（4）
耦合文献（0）

参考文献(6)

引证文献(4)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effects of Alloying Elements on Microstructure and Erosion Resistance of Fe-C-Cr Weld Surfacing Layer

参考文献(6)

引证文献(4)

用户提示