题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Surface Defects of Cold-Rolled Ti-IF Steel Sheets due to Non-Metallic Inclusions显示文摘Surface defects of the cold-rolled sheets of Ti-IF steel were studied and analyzed. After analyzing surface defects of cold-rolled sheets, such as shelling defects, holes and sliver defects by SEM/EDS, a variety of inclusions were found. In addition, the distribution of macro-inclusions in slabs was analyzed by MIDAS method. The results show the macroscopic inclusion bands of head slabs and normal slabs are in 1/8 slab thickness regions of both inner arc side and outer arc side. The formation process of the defects in the cold-rolled sheets was simulated with an experimental cold-rolling machine for comparison. The results show that there were three kinds of inclusions underneath the surface defects: Al2O3, SiO2 and particles from slag entrainment, which were the main reason for defect formation during cold rolling. | CUI Heng1, WU Hua-jie1, YUE Feng1, WU Wei-shuang1, WANG Min1, BAO Yan-ping1, CHEN Bin2, JI Chen-xi2 (1. Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China 2. Shougang Research Institute of Technology, Beijing 100043, China) | 2011 | Journal of Iron and Steel Research(International)2011，18，S2： | 8 |
| 2 | Extremely high-rate aqueous supercapacitor fabricated using doped carbon nanoflakes with large surface area and mesopores at near-commercial mass loading显示文摘在基于所有碳电极并且在良性的水的媒介操作而不是常规器官的电解质的 supercapacitor 完成令人满意的精力力量联合是主要挑战。为这个目的,我们制作了碳 nanoflakes (在厚度的 20-100 nm,在宽度的 5-m ) 包含一个大表面区域的无匹的联合(3,000 m 2sible 光活动被发现是 29.23 和 58.82 摩尔 ?? 挠潲獳氭湩敫 ? 牧灡敨敮 ?????? ?? 吗?? | Nan Mao Huanlei Wang Yang Sui Yongpeng Cui Jesse Pokrzywinski Jing Shi Wei Liu Shougang Chen Xin Wang David Mitlin | 2017 | Nano Research2017，10，5： | 5 |
| 3 | Final Temperature Prediction Model of Molten Steel in RH-TOP Refining Process for IF Steel Production显示文摘In order to precisely control the final temperature of molten steel in RH (Ruhrstahl Heraeus)-TOP blowing refining, the final temperature prediction models of molten steel in RH-TOP blowing refining process for Interstitial Free (IF) steel production were established under the condition of oxygen blowing and non-oxygen blowing respectively. The results show that the beginning molten steel temperature of refining and the amount of added scrap were influential factors, the baking temperature in vacuum chamber was a factor that had small influence. When the model was operated, the hitting probability was above 95% (under the condition of both oxygen blowing and non-oxygen blowing) of prediction deviation of ±10 ℃. The accuracy is analyzed. | WANG Yu-nan1, BAO Yan-ping1, CUI Heng2, CHEN Bin3, JI Chen-xi3 (1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 2. Engineering Research Institute, University of Science and Technology Beijing, Beijing 100083, China 3. Shougang Research Institute of Technology, Beijing 100041, China) | 2012 | Journal of Iron and Steel Research(International)2012，19，3： | 2 |
| 4 | Construction of High-Efficiency and Low-Cost Clean Steel Production System in Shougang Jingtang显示文摘This paper analyzes the technology for clean steel production in modern iron and steel plant,a philosophy with production efficiency,manufacturing cost and product performance in its core.It also makes a review on functions of high-efficiency,low-cost and high-quality steel products manufactured by the new generation iron and steel plant,in combination with the study on design of steelmaking-continuous casting process of Shougang Jingtang iron and steel Plant.By applying precise and dynamic design system to optimize and allocate systems and working procedures of hot metal pretreatment,converter smelting,secondary refining,continuous casting process,etc,a platform of high-efficiency,low-cost and high-quality clean steel production is built. | ZHANG Fu-ming,CUI Xing-chao,ZHANG De-guo(Beijing Shougang International Engineering Technology Co.,Ltd.,Beijing 100043,China) | 2011 | Journal of Iron and Steel Research(International)2011，18，S2： | 2 |
| 5 | Epitaxy of vertical ZnO nanorod arrays on highly (001)-oriented ZnO seed monolayer by a hydrothermal route显示文摘 | WU Weibing HU Guangda CUI Shougang | 2008 | Cryst Growth Des2008，8，11： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员