| 3 | Structure and Magnetic Properties of ZnO:Cr Prepared by CrIonIm plantation into ZnO Crystals显示文摘ZnO:Cr layer was prepared by Cr ion implantation into ZnO bulk crystals. The structural, optical, and magnetic properties of the ZnO:Cr layer were studied with X-ray diffraction, photoluminescence, and superconductor quantum interferometer, respectively. The ZnO:Cr layer implanted Cr with a dose of 5 10 16 cm 2 remained wurtzite structure and exhibited near-band-edge photoluminescence at 3.365 eV with full-width at half-maximum of 8.4 meV at 10 K. The magnetic measurement showed that the ferromagnetism changed at room temperature by different Cr concentration. For samples implanted to high doses, remanent magnetization reached 1.805 10 -4 emu/g and coercive field was 244.5 Oe. Hall effect measurement showed a decrease of the resistivity from 251.7 cmto 28.6 cmafter annealing at 800 ℃. The magnetism is interpreted by bound magnetic polarons, which were taken into account of the process that electrons were locally trapped by oxygen vacancies and occupied the orbitals that overlapped with d shell of neighboring Cr ions. | LIN Baozhu WANG Lingling Yuldashev Sh U FU Dejun KANG T W | 2013 | Wuhan University Journal of Natural Sciences2013，18，4： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员