|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Rheological behavior of semi-solid 7075 aluminum alloy at steady state显示文摘The further application of semi-solid processing lies in the in-depth fundamental study like rheological behavior. In this research, the apparent viscosity of the semi-solid slurry of 7075 alloy was measured using a Couette type viscometer. The effects of solid fraction and shearing rate on the apparent viscosity of this alloy were investigated under different processing conditions. It can be seen that the apparent viscosity increases with an increase in the solid fraction from 10% to 50%(temperature 620 oC to 630 oC) at steady state. When the solid fraction was fi xed, the apparent viscosity can be decreased by altering the shearing rate from 61.235 s-1 to 489.88 s-1 at steady state. An empirical equation that shows the effects of solid fraction and shearing rate on the apparent viscosity is fi tted:. The microstructure of quenched samples was examined to understand the alloy's rheological behavior. | Li Yageng Mao Weimin Zhu Wenzhi Yang Bin | 2014 | China Foundry2014，11，2： | 3 |
| 2 | Laser additive manufacturing of zinc:formation quality,texture,and cell behavior显示文摘Laser powder bed fusion(LPBF)makes it possible for biodegradable zinc(Zn)to be used to produce customized orthopedic implants.In this research,we investigate the impact of laser power and scanning speed on the development of surface quality,relative densification,and texture during LPBF of Zn implants.Increasing laser power was able to decrease melt viscosity and surface tension,which improved the metallurgical bonding between adjacent tracks.Uneven and twisted tracks also became continuous and straight.Scanning speed could controlmolten-pool temperature to restrain grain natural orientation,achieving various crystal orientations and a weakened texture.Importantly,it further avoided the thermal expansion and contraction caused by excessive energy storage and accumulation in the matrix,thus reducing the generation of high-dislocation density.As a result,by selecting a reasonable laser power and scanning speed,the LPBF parts exhibited a flat surface morphology and a high density over 99.5%.Their average hardness,mechanical strength,and elongation reached 50.2 HV,127.8 MPa,and 7.6%,respectively.Additionally,the parts displayed a moderate degradation rate and excellent osteogenic properties.All these results provide a basis for selecting process parameters to optimize the comprehensive properties of LPBF-processed Zn parts for biodegradable applications. | Mingli Yang Liuyimei Yang Shuping Peng Fang Deng Yageng Li Youwen Yang Cijun Shuai | 2023 | Bio-Design and Manufacturing2023，6，2： | 1 |
| 3 | Microstructure development and biodegradation behavior of additively manufactured Mg-Zn-Gd alloy with LPSO structure显示文摘Biodegradable magnesium(Mg)alloy has been considered as a new generation of orthopedic implant ma-terial.Nevertheless,local corrosion usually occurs since the severe micro-galvanic behavior amongα-Mg and precipitates,and results in too rapid degradation.In this study,porous Mg-Zn-Gd part was fabricated using laser additive manufacturing combined with solution heat treatment.During heat treatment,the precipitatedβ-(Mg,Zn)_(3) Gd phase dissolved inα-Mg,and reduced the energy threshold of stacking faults on basal planes,which finally triggered the formation of long period stacking ordered(LPSO)phase.The LPSO phases owned minor potential difference withα-Mg,thus causing less micro-galvanic corrosion ten-dency as compared toβ-(Mg,Zn)_(3) Gd phase.More importantly,they were uniformly distributed within theα-Mg grains and showed different orientations between adjacent grains.As a result,the LPSO-reinforced Mg-Zn-Gd tended to expand laterally during corrosion evolution,and achieved uniform degradation with a considerably reduced degradation rate of 0.34 mm/year.Moreover,in-vitro cell tests further proved its favorable biocompatibility.This work highlighted the additively manufactured Mg-Zn-Gd with LPSO structure showed great potential for orthopedic application. | Youwen Yang Chenrong Ling Yageng Li Shuping Peng Deqiao Xie Lida Shen Zongjun Tian Cijun Shuai | 2023 | Journal of Materials Science & Technology2023，，13： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员