| 3 | Microstructure and hardness of Mg-based composites reinforced with Mg_2Si particles显示文摘Magnesium powders were mechanically alloyed with SiO2 powder particles having different particle sizes using high-energy ball milling techniques under Ar atmosphere for 1 h. The powders were consolidated with cold pressing under 560 MPa. They were then sintered at 550°C for 45 min under Ar atmosphere. The composites obtained on the Mg-SiO2 system were investigated using the Archimedes principle, a differential scanning calorimeter, X-ray diffraction, optic microscopy, and scanning electron microscopy. For the mechanically alloyed powders, the solid-state reaction of the synthesis of Mg2Si and MgO progressed further during sintering of the materials. The results showed that the strengthening mechanisms were dependent on dispersion hardening of fine Mg2Si and MgO particulates dispersed homogeneously in the matrix. | Mustafa Aydin Cem zgür Osman San | 2009 | Rare Metals2009，28，4： | 0 |