| 1 | Effect of Pressure and Temperature on Phase Transformation and Properties of Titanium Aluminide Obtained through Reaction Synthesis显示文摘Reaction synthesis process has been used to develop γ titanium aluminide using elemental powders. Powder mixture of Ti-48 at. pct Al was prepared in ball mill and reaction synthesis was carried out in hot press with varying temperature and pressure. Titanium aluminide synthesized under high pressure and temperature resulted in better properties with respect to densification, homogenization response, mechanical properties and oxidation resistance as compared to that synthesized under low pressure and temperature. Al rich phases were observed in as-synthesized condition in all the experiments. However, some Ti rich phases were also found in high pressure-temperature synthesized samples. Density, hardness and tensile strength have been correlated with applied pressure through empirical relations. Variation in density with pressure is found to be logarithmic whereas hardness and tensile strength variation with pressure is polynomial. | R.K.Gupta Bhanu Pant Vijaya Agarwala R.C.Agarwala P.P.Sinha | 2010 | Journal of Materials Science & Technology2010，26，8： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员