| 2 | Microstructural evolution of TiAl base alloy during three-stepped thermo-mechanical treatment显示文摘A TiAl base alloy ingot with a height to diameter ratio of 2.2 was broken down by multiple step canned forging. The microstructures after every deformation and subsequent recrystallization were observed by optical microscopy. Results show that at the first step the reduction should be carefully controlled in case of double bulge and crack of the ingot. After the first annealing, recrystallization occurred at the deformed grain boundaries and inside the grain. The recrystallized microstructure is favorable for further deformation. After the second deformation and annealing, coarsening of the lamellae occurred and the microstructure became equiaxed. By the final deformation and subsequent recrystallization, the coarse lamellar colony can be refined to about 20 μm, and homogeneous microstructure was obtained from the ingot with a large initial height to diameter ratio. | LIU Yong,LIU Feng xiao,HUANG Bai yun,ZHOU Ke chao,ZHANG Chuan fu (State Key Lab for Powder Metallurgy, Central South University, Changsha 410083, China) | 2001 | Journal of Central South University of Technology2001，8，1： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员