题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Transformation of Laves phases and its effect on the mechanical properties of TIG welded Mg-Al-Ca-Mn alloys显示文摘The effects of Al content and Ca/Al mass ratio on the microstructure and mechanical properties of tungsten inert gas(TIG)welded Mg-2Ca-x Al-0.5Mn(x=0,1,5)alloy joints were studied in present work.Results showed that increasing Al content was effective in reducing the dendrite spacing at the fusion zone(FZ)edge.The Laves phases in the FZ and the heat-affected zone(HAZ)can be changed from Mg_(2)Ca to(Mg,Al)_(2)Ca with the decrease of Ca/Al ratio,and the(Mg,Al)_(2)Ca could be further transformed to Al_(2)Ca under welding thermal cycle.Furthermore,dynamic dissolution and precipitation of Laves phases and Al_(8)Mn_(5)phases occurred in the HAZ,resulting in a gradient microstructure and hardness peak in this area.The tensile properties of the joints were significantly improved with the increase of Al content,which was mainly due to the modification of Laves phases. | Sensen Chai Shiyu Zhong Qingshan Yang Daliang Yu Qingwei Dai Hehe Zhang Limeng Yin Gang Wang Zongxiang Yao | 2022 | Journal of Materials Science & Technology2022，，25： | 2 |
| 2 | Solid-state bonding process induced highly synergistic mechanical properties of 6061 Al alloy joint by shear deformation显示文摘Obtaining a highly synergistic mechanical property between joint and base metal(BM)in aluminum(Al)alloy is a chronic problem.In this work,shear bonding technology is applied to a commercial 6061 Al alloy.The results show that a flat and uniform joint interface is obtained.The joint presents a highly synergistic mechanical property compared with BM,whether after shear bonding or heat treatment.The joint coefficient reaches 95.6%after shear bonding and exceeds 100%after heat treatment,which is better than the traditional connection method of aluminum alloy.The high joint coefficient mainly originates from the well-linked joint and gradient grain structure.The gradient grain structure is beneficial to activate more slip systems to coordinate plastic deformation.Although the fine-grained structure is sacrificed after heat treatment,higher strength and joint coefficient are obtained due to the higher work hardening.This newly developed method has a large potential for application to the infinite rolling of Al alloy sheets and can also be used for Al alloy connection in automobile,aerospace,rail transportation,and other fields.The findings in this work can provide essential theoretical support and application reference for the shear connection of Al alloy. | Peng Peng Jian Su Qingsong He Ruinan Chen Sensen Chai Daliang Yu Qingwei Dai Jian Lu | 2023 | Journal of Materials Science & Technology2023，，33： | 0 |
| 3 | Stabilized multifunctional phase change materials based on carbonized Cu-coated melamine foam/reduced graphene oxide framework for multiple energy conversion and storage显示文摘The leakage of organic phase change materials(OPCMs)at temperatures above their melting point severely limits their large-scale application.The introduction of porous supports has been identified as an efficient leakageproofing method.In this study,a novel carbonized Cu-coated melamine foam(MF)/reduced graphene oxide(rGO)framework(MF/rGO/Cu-C)is constructed as a support for fabricating stabilized multifunctional OPCMs.MF serves as the supporting material,while rGO and Cu act as functional reinforcements.As a thermal energy storage material,polyethylene glycol(PEG)is encapsulated into MF/rGO/Cu-C through a vacuum-assisted impregnation method to obtain PEG@MF/rGO/Cu-C composite with excellent comprehensive performance.PEG@MF/rGO/Cu-C exhibits high phase change enthalpies of 148.3 J g^(-1)(melting)and 143.9 J g^(-1)(crystallization),corresponding to a high energy storage capability of 92.7%.Simultaneously,MF/rGO/Cu-C endues the composite with an enhanced thermal conductivity of 0.4621Wm^(-1) K^(-1),which increases by 463%compared to that of PEG@MF.Furthermore,PEG@MF/rGO/Cu-C displays great light-to-thermal and electric-to-thermal conversion capabilities,thermal cycle stability,light-tothermal cycle stability,and shape stability,showing promising application prospects in different aspects. | Zhicong Hu Yongjin Zou Cuili Xiang Lixian Sun Fen Xu Menghe Jiang Sensen Yu | 2022 | Carbon Energy2022，4，6： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员