2篇
您的检索式：作者名="Shougang Duan"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel with Sulfate-Reducing Bacteria显示文摘Cathodic protection is a very effective method to protect metals, which can form calcareous deposits on metal surface. Research on the interrelationship between fouling organism and calcareous deposits is very important but very limited, especially sulfate-reducing bacteria(SRB). SRB is a kind of very important fouling organism that causes microbial corrosion of metals. A study of the influence of calcareous deposit on corrosion behavior of Q235 carbon steel in SRB-containing culture medium was carried out using electrochemical impedance spectroscopy(EIS), scanning electron microscopy(SEM) and surface spectroscopy(EDS). The calcareous deposit was formed with good crystallinity and smooth surface under the gradient current density of -30 μA cm^(-2) in natural seawater for 72 h. Our results can help elucidate the formation of calcareous deposits and reveal the interrelationship between SRB and calcareous deposits under cathodic protection. The results indicate that the corrosion tendency of carbon steel was obviously affected by Sulfate-reducing Bacteria(SRB) metabolic activity and the calcareous deposit formed on the surface of carbon steel under cathodic protection was favourable to reduce the corrosion rate. Calcareous deposits can promote bacterial adhesion before biofilm formation. The results revealed the interaction between biofouling and calcareous deposits, and the anti-corrosion ability was enhanced by a kind of inorganic and organic composite membranes formed by biofilm and calcareous deposits. | ZHANG Jie LI Xiaolong WANG Jiangwei XU Weichen DUAN Jizhou CHEN Shougang HOU Baorong | 2017 | Journal of Ocean University of China2017，16，6： | 1 |
| 2 | Effects of V Addition on Microstructural Evolution and Mechanical Properties of AlCrFe_(2)Ni_(2) High‑Entropy Alloys显示文摘The effects of vanadium addition on the microstructural evolution and mechanical properties of AlCrFe_(2)Ni_(2) high-entropy alloy(HEA)were investigated.The results showed that the AlCrFe_(2)Ni_(2)V_(0.2) HEA was composed of FCC phase,disordered BCC phase,and ordered BCC(B2)phase.With the increase in vanadium content,the formation of FCC phase was inhibited,and a transition from FCC phase to BCC phase occurred.The FCC phase disappeared completely when the value of x exceeds 0.4 in AlCrFe_(2)Ni_(2)V_(x) HEAs.Besides,the amplitude-modulated microstructure morphology transformed from a B2 phase matrix with dispersed BCC nano-phase into an alternating interconnected B2 and BCC phases.Vanadium element has the function of stabilizing BCC phase and B2 phase in AlCrFe_(2)Ni_(2)V_(x) alloys.The hardness of AlCrFe_(2)Ni_(2)V_(x) alloys increased from HV 332.4 to HV 590.7,while the yield strength increased from 765 to 1744.6 MPa with increasing vanadium content,which was mainly due to the decreasing content of FCC phase and the solid solution strengthening of vanadium element.At the same time,the compression ratio of the alloys decreased with the disappearance of the FCC phase.Among the alloys,the AlCrFe_(2)Ni_(2)V_(0.2) alloy possessed the most excellent comprehensive mechanical properties with yield strength,fracture strength,and compressive ratio 1231.1,2861.9 MPa,and 44.5%,respectively. | Shougang Duan Qian Zhang Wenxuan Li Yong Dong Beibei Jiang Shichao Liu Chuanqiang Li Zhengrong Zhang | 2023 | Acta Metallurgica Sinica(English Letters)2023，36，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员