2篇
您的检索式：作者名="Tangxia Yu"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Effect of chemical composition on the element distribution,phase composition and calcification roasting process of vanadium slag显示文摘The chemical composition of vanadium slag significantly affects its element distribution and phase composition,which affect the subsequent calcification roasting process and vanadium recovery.In this work,seven kinds of vanadium slags derived from different regions in China were used as the raw materials to study the effects of different components on the vanadium slag’s elements distribution,phase composition,calcification roasting,and leaching rate of major elements using scanning electron microscope,X-ray diffraction analysis,and inductively coupled plasma-optical emission spectroscopy.The results show that the spinel phase is wrapped with silicate phase in all vanadium slag samples.The main elements in the spinel phase are Cr,V,and Ti from the interior to the exterior.The size of spinel phase in low chromium vanadium slag is larger than the other vanadium slags with higher chromium contents.The spinel phase of high-calcium and high-phosphorus vanadium slag is more dispersed.The strongest diffraction peak of vanadium spinel phase in the vanadium slag migrates to a higher diffraction angle,and(Fe_(0.6)Cr_(0.4))_(2)O_(3)is formed after calcification roasting as the chromium content increased.A large amount of Ca_(2)SiO_(4)is produced because excess Ca reacts with Si in high-calcium and high-phosphorus vanadium slag.The vanadium leaching rate reaches 88%in some vanadium slags.The chromium leaching rate is less than 5%in all vanadium slags.The silicon leaching rate of high-calcium and high-phosphorus vanadium slag is much higher than that of the other slags.The leaching rate of manganese is higher than 10%,and the leaching rates of iron and titanium are negligible. | Tangxia Yu Tao Jiang Jing Wen Hongyan Sun Ming Li Yi Peng | 2022 | International Journal of Minerals,Metallurgy and Materials2022，29，12： | 1 |
| 2 | High-chromium vanadium-titanium magnetite all-pellet integrated burden optimization and softening-melting behavior based on flux pellets显示文摘High-chromium vanadium-titanium magnetite(HVTM)is a crucial polymetallic-associated resource to be developed.The allpellet operation is a blast furnace trend that aims to reduce carbon dioxide emissions in the future.By referencing the production data of vanadium-titanium magnetite blast furnaces,this study explored the softening-melting behavior of high-chromium vanadium-titanium magnetite and obtained the optimal integrated burden based on flux pellets.The results show that the burden with a composition of 70wt%flux pellets and 30wt%acid pellets exhibits the best softening-melting properties.In comparison to that of the single burden,the softening-melting characteristic temperature of this burden composition was higher.The melting interval first increased from 307 to 362℃and then decreased to 282℃.The maximum pressure drop(ΔPmax)decreased from 26.76 to 19.01 kPa.The permeability index(S)dropped from 4643.5 to 2446.8 kPa·℃.The softening-melting properties of the integrated burden were apparently improved.The acid pellets played a role in withstanding load during the softening process.The flux pellets in the integrated burden exhibited a higher slag melting point,which increased the melting temperature during the melting process.The slag homogeneity and the TiC produced by over-reduction led to the gas permeability deterioration of the single burden.The segregation of the flux and acid pellets in the HVTM proportion and basicity mainly led to the better softening-melting properties of the integrated burden. | Bojian Chen Tao Jiang Jing Wen Guangdong Yang Tangxia Yu Fengxiang Zhu Peng Hu | 2024 | International Journal of Minerals,Metallurgy and Materials2024，31，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员