| 1 | Thermal Deformation Behavior and Processing Map of a Novel CrFeNiSi_(0.15)Medium Entropy Alloy显示文摘The thermal deformation behavior of a novel CrFeNiSi_(0.15)medium entropy alloy(MEA)was studied via isothermal compression experiments,with the processing parameter range of 900–1200℃and 0.001–1 s^(−1).According to experimental data,the modified constitutive equation had been obtained,which precisely predicted the flow behavior of CrFeNiSi_(0.15)MEA during thermal deformation.At the same time,the processing map was established on the basis of the dynamic material model(DMM)theory.According to the map,the optimal processing parameters were determined at 1130–1200℃/0.06–1 s−1,under which the power dissipation efficiency could reach above 34%.The peak efficiency was above 38%,which occurred at 1200℃/1 s^(−1).In such parameter,complete dynamic recrystallization(DRX)also occurred.The flow instability of CrFeNiSi_(0.15)MEA was estimated to occur at 900–985℃/0.12–1 s^(−1),which was shown as grain boundaries cracking.Furthermore,both the continuous DRX(CDRX)and discontinuous DRX(DDRX)occurred simultaneously during thermal deformation.Meanwhile,some twins were also newly formed during DRX process,most of which were primary twins.The occurrence of twinning was beneficial to promote the development of DRX behavior. | Hongbin Zhang Kang Chen Zhongwei Wang Haiping Zhou Chengcheng Shi Shengxue Qin Jie Liu Tingjun Lv Jian Xu | 2023 | Acta Metallurgica Sinica(English Letters)2023，36，11： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员