| 1 | PHASE TRANSFORMATION AND CHARACTERISTICS IN FRECKLE AREAS FOR INCONEL 625 SUPERALLOY显示文摘The freckle formation and their phase characterizatics in freckle areas were investigated by means of microstructure analysis approaches and a thermodynamic equilibrium phase calculation method in an Inconel 625 alloy.These results show that in freckle areas a large number of M6C, MC, Laves and δ phases precipitate in grain boundaries even within grain due to the enrichment and segregation of Mo and Nb during solidification, which results in almost of these freckle areas covered by these complex precipitated phases and induces small grains in freckle areas.Equilibrium phase and liquid segregation calculation can give a reasonable interpretation of the freckle feature for this alloy. | J.X.Dong M.C.Zhang Y.P.Zeng X.S.Xie | 2005 | Acta Metallurgica Sinica(English Letters)2005，18，1： | 11 |
| 2 | SEM in-situ investigation on fatigue cracking behavior of P/M Rene95 alloy with surface inclusions显示文摘 | X.S.Wang L.N.Zhang Y.P.Zeng X.S.Xie | | 0，，13： | 1 |
| 3 | CREEP CRACK GROWTH BEHAVIOR OF ALLOY 718 DURING HIGH TEMPERATURE EXPOSURE显示文摘Alloy 718 is a precipitation strengthened nickel-based superalloy based on the precipitation of γ″-Ni3Nb (DO22 structure) and γ′-Ni3(Al,Ti) (L12 structure) phases. Creep crack growth rate (CCGR) was investigated after high temperature exposure at 593, 650 and 677℃ for 2000h in Alloy 718. In addition to the coalescence of γ′/ γ″ and the amount increasing of δ phase, the existence of a bcc chromium enriched α-Cr phase was observed by SEM, and the weight fraction of α-Cr and other phases were determined by chemical phase analysis methods. The CCGR behavior and regulation have been analyzed by means of strength and structure analysis approaches. The experimental results show higher the exposure temperature and longer the exposure time, lower the CCGR. This is probably attributed to the interaction of material softening and brittling due to complex structure changes during high temperature exposure. Therefore, despite α-Cr phase formation and amount enhancement were run in this test range. It seems to us a small amount of α-Cr will be not harmful for creep crack propagation resistance, which is critical for disk application in aircraft and land-based gas turbine. | J.X.Dong M.C.Zhang Y.P.Zeng X.S.Xie | 2005 | Acta Metallurgica Sinica(English Letters)2005，18，2： | 0 |
| 4 | FRECKLE FORMATION AND CHARACTERIZATION OF A Ni-Cr-Mo-Fe-W ALLOY显示文摘The freckle formation and their phase characterization in freckle areas were investigated by means of microstructure analysis approaches and a thermodynamic equilibrium phase calculation method in a Ni-Cr-Mo-Fe-W alloy. These results show that in freckle areas a large number of M6 C, μ and P phases precipitate in grain boundaries even within grain due to the enrichment and segregation of Mo and C during solidification, which results in small grains in freckle areas. Equilibrium phase and liquid segregation calculation can give an reasonable interpretation of the freckle feature for this alloy. | J.X.Dong M.C.Zhang Y.P.Zeng X.S.Xie | 2004 | Acta Metallurgica Sinica(English Letters)2004，17，4： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员