| 1 | Microstructure Dependent Fatigue Cracking Resistance of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy显示文摘Fatigue cracking behavior from a notch was investigated at room temperature for Ti-6.5Al-3.5Mo-1.5Zr-0.3Si(TC11) alloys with four different microstructures obtained at different cooling rates from the β transus temperature.It was found that the alloy with lamellar structures consisting of α/β lamellae or acicular α' martensite laths had a higher fatigue crack initiation threshold from the notch,while the bimodal structure with coarse α grain had a lower fatigue cracking resistance.The alloy with α/β lamellar structure showed a higher fatigue crack growth resistance.The length scales of the microstructures were characterized to correlate with fatigue cracking behavior.Fatigue cracking mechanism related to microstructures was discussed. | Z.M. Song L.M. Lei B. Zhang X. Huang G.R Zhang | 2012 | Journal of Materials Science & Technology2012，28，7： | 7 |