Controllable synthesis of high loading LiFePO_4/C nanocomposites using bimodal mesoporous carbon as support for high power Li-ion battery cathodes

查看全文 作　　者：Fei [1]Cheng;Duo [1]Li;Anhui [1]Lu;Wencui [1]Li 高影响力作者 机构地区：[1]State Key Laboratory of Fine Chemicals, School of Chemical Engineering, Faculty of Chemical, Environmental and Biological Science and Technology, Dalian University of Technology高影响力机构 出　　处：《Journal of Energy Chemistry》索引2013年第22卷第6期,共7页高影响力期刊 基　　金：supported by the National Natural Science Foundation of China (NSFC 21103184);the Ph.D.Programs Foundation (20100041110017) of Ministry of Education of China;the Fundamental Research Funds for the Central Universities 摘　　要：Mesoporous LiFePO4/C composites containing 80 wt% of highly dispersed LiFePO4 nanoparticles(4-6 nm) were fabricated using bimodal mesoporous carbon(BMC) as continuous conductive networks. The unique pore structure of BMC not only promises good particle connectivity for LiFePO4, but also acts as a rigid nano-confinement support that controls the particle size. Furthermore, the capacities were investigated respectively based on the weight of LiFePO4 and the whole composite. When calculated based on the weight of the whole composite, it is 120 mAh·g-1at 0.1 C of the high loading electrode and 42 mAh·g-1at 10 C of the low loading electrode. The electrochemical performance shows that high LiFePO4 loading benefits large tap density and contributes to the energy storage at low rates, while the electrode with low content of LiFePO4 displays superior high rate performance, which can mainly be due to the small particle size, good dispersion and high utilization of the active material, thus leading to a fast ion and electron diffusion. 关 键 词：LIFEPO4 HIGH loading fast ion diffusion HIGH rate performance LITHIUM-ION batteries
相关文献

参考文献(10)

引证文献(2)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费