2篇
您的检索式：作者名="Benoit Ndiwe"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Matrix Assisted Laser Desorption Ionization Time of Flight(MALDI-TOF)-Mass Spectrometry and^(13)C-NMR-Identified New Compounds in Paraberlinia bifoliolata(Ekop-Beli)Bark Tannins显示文摘Extracts of plant origin,particularly tannins,are attracting growing interest for the sustainable development of materials in the industrial sector.The discovery of new tannins is therefore necessary.The aim of this work was to contribute to the understanding of the properties of Paraberlinia bifoliolata tannin by Matrix Assisted Laser Desorption Ionization Time of Flight Mass Spectroscopy MALDI-TOF/MS and Carbon 13 Nuclear Magnetic Resonance(13C NMR).The chemical composition of tannin extracted from Paraberlinia bifoliolata bark was determined,as was the mechanical strength of the resin hardened with Acacia nilotica extracts.Yield by successive water extraction was 35%.MALDI-TOF/MS analysis revealed the presence of three new compounds in this tannin,previously unknown in this family of extracts.These are 3-hydroxyproline acid,N-methyl-4-hydroxypipecolic acid and N-methyl-5-dihydroxypipecolic acid.The identification of the above molecules means that this tannin can be used for industrial applications,as a resin in the manufacture of particleboard and in the formulation of green corrosion inhibitors.This information is reinforced by 13C NMR spectrometry,which indicates the presence of several polyflavonoid units,confirming the condensed nature of the tannin.Thermomechanical analysis of the resin formed by the purified tannin of Paraberlinia bifoliolata to which a vegetal biohardener has been added provided a Modulus of Elasticity(MOE)value of 4840 MPa at 150°C,confirming its possible use as a binder resin in the manufacture of wood panels as well as for the formulation of a corrosion inhibitor. | Liliane Nga Benoit Ndiwe Achille Bernard Biwolé Antonio Pizzi Jean Jalin Eyinga Biwole Joseph Zobo Mfomo | 2024 | Journal of Renewable Materials2024，12，3： | 0 |
| 2 | Desorption Behavior and Thermogravimetric Analysis of Bio-Hardeners显示文摘In this work,the thermal degradation and drying of bio-hardeners are investigated.Four bio-hardeners based on exudates of Senegalia senegal,Vachellia nilotica,Vachellia seyal,and Acacia siebteriana were analyzed by FTIR and thermogravimetric analysis,and a desorption study was also conducted.The analysis by infrared spectroscopy indicates the existence of oligomers of different types all giving 5-hydroxy-2-hydroxymethylfuran and 2,5-dihydroxymethylfuran which are then the real hardening molecules.The pyrolysis of these extracts reveals three main regions of mass loss,a first region is located between 25℃and 110℃reflecting the loss of water from the adhesive and the formation of some traces of volatile organic compounds such as CO_(2)and CO,a second zone characterized by the release of CO,CO_(2)and CH4 gases with peaks between 110°and 798.8℃.At the end of the analysis,about 22%of the initial mass remains undecomposed,this mass corresponds to the rigid segments of the bio-hardener which are not completely decomposed. | Benoit Ndiwe Antonio Pizzi Hubert Chapuis Noel Konai Lionel Karga Pierre Girods Raidandi Danwe | 2022 | Journal of Renewable Materials2022，10，8： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员