| 1 | Er^(3+)-activated silica inverse opals synthesized by the solgel method显示文摘We present the details of the sol-gel processing used to realize inverse silica opal,where the silica was activated with 0.3 mol% of Er3+ ions. The template(direct opal) was obtained assembling polystyrene spheres of the dimensions of 260 nm by means of a vertical deposition technique. The Er3+-activated silica inverse opal was obtained infiltrating,into the void of the template,the silica sol doped with Er3+ ions and subsequently removing the polystyrene spheres by means of calcinations. Scanning electron microscope showed that the inverse opals possess a fcc structure with a air hollows of about 210 nm and a photonic band gap,in the visible range,was observed from reflectance measurements. Spectroscopic properties of Er3+-activated silica inverse opal were investigated by luminescence spectroscopy,where,upon excitation at 514.5 nm,an emission of 4I13/2 → 4I15/2 of Er3+ ions transition with a 21 nm bandwidth was observed. Moreover the 4I13/2 level decay curve presents a single-exponential profile,with a measured lifetime of 18 ms,corresponding a high quantum efficiency of the system. | A. Chiappini C.Armellini A. Chiasera Y. Jestin M. Ferrari M. Mattarelli M. Montagna E. Moser C. Tosello L. Zampedri G. Nunzi Conti S. Pelli R. M. Almeida G. C. Righini | 2007 | Optoelectronics Letters2007，3，3： | 2 |
| 2 | Effect of Yb^(3+) concentration on Er^(3+) luminescence properties of sol-gelderived silica-alumina xerogels显示文摘Er3+/Yb3+ co-doped silica-alumina monolithic xerogels were prepared with the same concentration on 2 000 Er/Si ppm and 6 000 Al/Si ppm.The Yb/Si content was varied from 0 to 4 000 ppm.Densification of the samples was achieved by thermal treatment in air at 950 ℃ for 120 hours with a heating rate 0.1 ℃/min.Photoluminescence spectroscopy was used to obtain information about the effective excitation efficiency of Er3+ ions by co-doping with Yb 3+ ions.The infrared-to-visible up-conversion luminescence has been investigated upon continuous wave excitation at 980 nm.The samples exhibit red,green and blue up-conversion emission.It is found that the intensity of up-conversion luminescence increases with increasing Yb3+ doping concentration.An opposite behavior is observed for the 4I13/2 luminescence of the Er3+ ions. | K.Tran Ngoc H.Pham Thanh C.Nguyen Duc C.Armellini A.Chiasera M.Ferrari Y.Jestin M.Montagna E.Moser S.Pelli G.C.Righini | 2006 | Optoelectronics Letters2006，2，5： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员