| 1 | Effect of processing parameters on the microstructure and mechanical properties of TiAl/Ti_(2)AlNb laminated composites显示文摘In order to improve the intrinsic brittleness of TiAl alloys,Ti_(2)AlNb alloys with outstanding ductility and toughness at room temperature,and good high-temperature performance are competitive candidates in constructing the TiAl-based laminated composites.In this work,TiAl/Ti_(2)AlNb laminated composites are successfully synthesized by vacuum hot pressing combined with the foil-foil(sheet)metallurgy.Under the pressure of 65 MPa,different holding time and temperature of hot pressing are tried and the optimized fabrication parameter is acquired as 1050℃/120 min/65 MPa.Along with the changes of processing parameters,the defect,microstructure,interface,phase transformation and the corresponding mechanical properties are detailly discussed.The results show that the TiAl/Ti_(2)AlNb laminated composite fabricated at 1050℃ for 2 h achieves a good metallurgical interface bonding.The corresponding interface microstructure is composed of region I and region II.The region I consists of O,α_(2)and B2/βphase,and region II is made up ofα2.Subsequently,the tensile tests indicate that the composite synthesized at 1050℃ for 2 h possesses a maximum strength of 812 MPa and a total elongation of 1.31%at room temperature,and a strength of 539.71 MPa and the highest total elongation of 10.34%at 750℃.The well synergistic deformation ability between the interface and the two base alloys endows the composite an excellent tensile performance.Moreover,the composite processed at 1050℃ for 2 h behaves the best fracture toughness in both arrester orientation and divider orientation with the value of 32.6 MPa.m^(1/2)and 30.1 MPa.m^(1/2),respectively.The Ti_(2)AlNb alloy in the laminated structure effectively release the stress around the crack tip and plays a role in toughening.Further,crack deflection,crack bridging,crack blunting and fragmentation also make contributions to enhance the fracture toughness of the laminated composites. | Donghai Li Binbin Wang Liangshun Luo Xuewen Li Yanjin Xu BinQiang Li Diween Hawezy Liang Wang Yanqing Su Jingjie Guo Hengzhi Fu | 2022 | Journal of Materials Science & Technology2022，，14： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员