| 1 | 添加晶粒细化剂硅对Ti-6Al-4V合金组织和性能的影响(英文)显示文摘采用真空感应凝壳熔炼工艺在石墨模中制备Ti-6Al-4V和Ti6Al4V0.5Si两种钛合金。将硅作为一种晶粒细化剂加入到Ti-6Al-4V合金中,考察添加硅对铸态和模锻态Ti-6Al-4V合金组织和性能的影响。铸态合金先在900°C下进行热模锻处理,然后分别进行两种不同的热处理。一种是将模锻样品在1050°C下保温30min,然后水淬以获得细小的层片状组织;另一种是将模锻件在1050°C下保温30min,然后再在800°C下保温30min,以获得粗大的层片状组织。Ti6-Al-4V合金中添加0.5%Si后,铸态合金的晶粒尺寸从627μm减小到337μm,其极限抗拉强度增加约25MPa。具有细小、层片状组织的Ti-6Al-4V0.5Si合金的最大极限抗拉强度为1380MPa,在Hank溶液和NaCl溶液中的腐蚀速度分别为1.35×106和5.78×104mm/a。Ti-6Al-4V合金中添加0.5%Si后,在低滑动速度下的磨损率降低50%,在高滑动速度下的磨损率降低约73%。 | Khaled M.IBRAHIM Abdel Hamied HUSSEIN Mohamed ABDELKAWY | 2013 | Transactions of Nonferrous Metals Society of China2013，23，7： | 2 |
| 2 | Highly transmitted silver nanowires-SWCNTs conductive flexible film by nested density structure and aluminum-doped zinc oxide capping layer for flexible amorphous silicon solar cells显示文摘Indium tin oxide(ITO)is widely used in transparent conductive films(TCFs);however,several disadvan-tages,such as high cost and toxicity of indium,limit its applications.Therefore,it is necessary to develop other materials that can replace ITO.Silver nanowires or single walled carbon nanotubes(SWCNTs)have attracted considerable interest owing to their unique electrical,optical,and thermal stabilities,and thus,they are ideal for transparent electrodes for flexible or stretchable devices.In this study,we develop a novel architecture of composite TCFs on a polyethylene naphthalate(PEN)flexible substrate.Herein,the silver nanowires-SWCNTs films with nested density structure were fabricated through ultrasonic spraying technology by varying the spraying width.For achieving enhanced transmittance,we combined the larger irregular grids and holes with fewer nanowires stacked in the longitudinal direction,more optical chan-nels,and good carrier transport.Thereafter,aluminum-doped zinc oxide(AZO)was used as capping to the structure for enhancing the optical properties of the TCFs.The silver nanowires-SWCNTs/AZO(ASA)bilayer was obtained in the optimized architecture,which showed superior optoelectronic performance to that shown by commercial ITO with a high optical transmittance of 92%at the wavelength of 550 nm and low sheet resistance of 17/sq.In the specially structured conductive film,the significant improvement in the transmittance and uniformity of the sheet resistance was attributed to the effective nanowire junc-tion contact compared to that in ordinary structure of silver nanowires,which reduced the mean density of small clusters of nanowires.Compared with the silver nanowires-SWCNTs films,the ASA bilayer film exhibited excellent resistance to boiling,mechanical bending(10,000 cycles),and CO_(2)plasma.Moreover,the sheet resistance of ASA changed slightly after the tape tests,thereby illustrating a strong adhesion to the PEN substrate after the enclosure of AZO.Meanwhile,the AZO capping layer can enhance the op-tical transmittance between 600 and 1500 nm.In addition,the amorphous silicon photovoltaic devices with flexible ASA TCFs exhibited a power conversion efficiency(PCE)of 8.67%.After bending for 3000 times,the PCE was decreased to 8.20%,thereby demonstrating the potential of developed films to replace traditional ITO. | Shunliang Gao Xiaohui Zhao Qi Fu Tianchi Zhang Jun Zhu Fuhua Hou Jian Ni Chengjun Zhu Tiantian Li Yanlai Wang Vignesh Murugadoss Gaber A.M.Mersal Mohamed M.Ibrahim Zeinhom M.El-Bahy Mina Huang Zhanhu Guo | 2022 | Journal of Materials Science & Technology2022，，31： | 2 |
您所在的机构暂未开通此部分的功能，请联系管理员