2篇
您的检索式：作者名="Songjin Ko"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Remarkable N_(2)-selectivity enhancement of NH_(3)-SCR over HPMo modified MnCo-BTC@SiO_(2) catalyst显示文摘In this work,the phosphomolybdate(HPMo)modification strategy was applied to improve the N_(2) selectivity of Mn Co-BTC@SiO_(2)catalyst for the selective catalytic reduction of NO_(x),and further,the mechanism of HPMo modification on enhanced catalytic performance was explored.Among Mn Co-BTC@SiO_(2-x) catalysts with different HPMo concentrations,Mn CoBTC@SiO_(2)-0.75 catalyst exhibited not only the highest NH_(3)-SCR performance(95% at 200-300℃)but also the best N_(2)selectivity(exceed 80% at 100-300℃)due to the appropriate redox capacity,greater surface acidity.X-ray photoelectron spectrometer(XPS)and temperature programmed reduction of H_(2)(H_(2)-TPR)results showed that the modification with HPMo reduced the oxidation-reduction performance of the catalyst due to electron transfer from Mo^(5+)to Mn^(4+)/Mn^(3+)and prevent the excessive oxidation of ammonia adsorption species.NH_(3)temperature-programmed desorption of(NH_(3)-TPD)results showed that the modification with HPMo could significantly improve the surface acidity and NH_(3)adsorption,which enhance the catalytic activity and N_(2)selectivity.In-situ diffused reflectance infrared Fourier transform spectroscopy(in-situ DRIFTS)revealed that modification with HPMo increased significantly the amount of adsorbed NH_(3)species on the Bronsted acid site and C_(B)/C_(L),it suppressed the production of N_(2)O by inhibiting the production of NH species,the deep dehydrogenation of ammonia adsorption species.This study provided a simple design strategy for the catalyst to improve the low-temperature catalytic performance and N_(2)selectivity. | Songjin Ko Xiaolong Tang Fengyu Gao Honghong Yi Hengheng Liu Ning Luo | 2024 | Journal of Environmental Sciences2024，，4： | 0 |
| 2 | Low-temperature NH_(3)-SCR performance of a novel Chlorella@Mn composite denitrification catalyst显示文摘The synthesis process of conventional Mn-based denitrification catalysts is relatively complex and expensive.In this paper,a resource application of chlorella was proposed,and a Chlorella@Mn composite denitrification catalyst was innovatively synthesized by electrostatic interaction.The Chlorella@Mn composite denitrification catalyst prepared under the optimal conditions(0.54 g/L Mn^(2+)concentration,20 million chlorellas/mL concentration,450℃ calcination temperature)exhibited a well-developed pore structure and large specific surface area(122 m^(2)/g).Compared with MnOx alone,the Chlorella@Mn composite catalyst achieved superior performance,with~100%NH_(3)selective catalytic reduction(NH_(3)-SCR)denitrification activity at 100-225℃.The results of NH_(3)temperature-programmed desorption(NH_(3)-TPD)and H_(2)temperature-programmed reduction(H_(2)-TPR)showed that the catalyst had strong acid sites and good redox properties.Zeta potential testing showed that the electronegativity of the chlorella cell surface could be used to enrich with Mn^(2+).X-ray photoelectron spectroscopy(XPS)confirmed that Chlorella@Mn had a high content of Mn^(3+)and surface chemisorbed oxygen.In-situ diffuse refectance infrared Fourier transform spectroscopy(in-situ DRIFTS)experimental results showed that both Langmuir-Hinshelwood(L-H)and Eley-Rideal(E-R)mechanisms play a role in the denitrification process on the surface of the Chlorella@Mn catalyst,where the main intermediate nitrate species is monodentate nitrite.The presence of SO_(2)promoted the generation and strengthening of Bronsted acid sites,but also generated more sulfate species on the surface,thereby reducing the denitrification activity of the Chlorella@Mn catalyst.The Chlorella@Mn composite catalyst had the characteristics of short preparation time,simple process and low cost,making it promising for industrial application. | Hengheng Liu Fengyu Gao Songjin Ko Ning Luo Xiaolong Tang Erhong Duan Honghong Yi Yuansong Zhou | 2024 | Journal of Environmental Sciences2024，，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员