2篇
您的检索式：作者名="Yunda DONG"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Development of microstructural inhomogeneity in multi-pass flow forming of TA15 alloy cylindrical parts显示文摘Revealing the development of microstructural inhomogeneity in the multi-pass flow forming of titanium alloy components is of great significance to the microstructure control and property tailoring.To this end,the microstructural inhomogeneity of TA15 alloy spun cylindrical parts was analyzed based on the deformation history.The results indicate that the material underwent significant compressive strain in the normal direction(ND),tension strain in the rolling and circumferential directions(RD and CD),while tension strain in the CD is slightly small due to the limited material flow in this direction.These strain characteristics make the microstructure,especially the primary a(ap),present different morphologies in the different planes of the part.Meanwhile,the combined effects of inhomogeneous deformation and temperature distribution in the ND also cause the inhomogeneity of microstructure morphology and parameters in this direction.Quantitative analyses show that with the forming pass increasing,the aspect ratio of apincreases most in the normal-rolling plane,then in the normal-circumferential plane and least in the circumferential-rolling plane,whereas apcontent decreases in an opposite trend.Along the ND,the aspect ratio and content of apis relatively high in the outer and inner surface areas but lowest in the central area,and these inhomogeneous characteristics can be gradually diminished with the forming pass increasing.Furthermore,the variation of hardness inhomogeneity factor indicates that a four-pass forming with the total reduction ratio of 63%could obtain a homogenous microstructure along the ND of the TA15 alloy spun cylindrical part. | Xianxian WANG Pengfei GAO Mei ZHAN Ke YANG Yunda DONG Yukun LI | 2020 | Chinese Journal of Aeronautics2020，33，7： | 3 |
| 2 | Effect of blank quenching on shear spinning forming precision of 2219 aluminum alloy complex thin-walled components显示文摘The quenching-spinning(Q-S)process,i.e.,shear spinning after blank quenching,has been increasingly utilized to form 2219 aluminum alloy complex thin-walled components.However,the changes in material property,shape and stress of the blanks after quenching will affect the spin-ning forming precision.In this study,the rules and mechanisms of these effects are investigated based on a combined finite element(FE)model including blank quenching and component spinning process.The results indicate that the increase of material strength and the existence of distortion of the quenched blank lead to a notable increase in the non-uniformity of the circumferential compres-sive stress in the spinning area and the increase of the flange swing height during spinning.These changes result in an increase in the wall thickness and component-mandrel gap of the components.The quenching residual stress has little effect on wall thickness and roundness but can noticeably reduce the component-mandrel gap.This is because that the existence of quenching residual stress of the blank can lead to the decrease of the maximum circumferential compressive stress of the workpiece in spinning and an obvious drop in the maximum compressive stress after reaching the stress peak.Quenching distortion is the main factor affecting the roundness.Moreover,the opti-mized installation way of the blank for spinning is obtained. | Zhixin LI Mei ZHAN Xiaoguang FAN Yunda DONG Luopeng XU | 2023 | Chinese Journal of Aeronautics2023，36，4： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员