查看全文 作　　者：Shanwu Yang, Chengjia Shang,Xinlai He, Xuemin Wang, Yi Yuan (Material Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China)

出　　处：《Journal of University of Science and Technology Beijing》索引2001年第8卷第2期,共4页

摘　　要：The stability of ultra-fine microstructure during tempering at 650℃ was investigated on a Nb-containing steel. The steel had undergone 5 passes controlled rolling, then was relaxed (air cooled) to 730 ℃ and cooled in water The evolution of microstructure was that, in early stage of tempering, no obvious change was detected by means of optical microscopy while dislocation cells were formed inside bainitic laths. With further tempering, bainitic laths started to coalesce in some regions. Finally, polygonal ferrite was formed while hardness decreased dramatically. Some samples taken from the same primary plate were reheated at 930 ℃for 0.5 h followed by quenching into water before tempering. Despite their lower original hardness, the reheated samples softened faster during tempering. Ferrite was quickly formed in the reheated samples. These results indicate that the evolution of microstructures towards equilibrium during tempering of the steel is mainly determined by whether dislocations are pinned rather than the dislocation density. 关键词：microalloyed steel BAINITE TEMPERING

相关文献

参考文献（2）
引证文献（26）
耦合文献（0）

参考文献(2)

引证文献(26)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Stability of Ultra-fine Microstructures during Tempering

参考文献(2)

引证文献(26)

用户提示