Synthesis of defect-rich hierarchical sponge-like TiO2 nanoparticles and their improved photocatalytic and photoelectrochemical performance

查看全文 作　　者：Qizhi [1]Tian;Yajun [1]Ji;Yiyi [1]Ojan;Abulikemu [2]Abulizi

机构地区：[1]College of Science,University of Shanghai for Science and Technology,Shanghai,200093,China;[2]College of Chemistry and Chemical Engineering,Xinjiang University,Urumqi,830046,China

出　　处：《Frontiers of Materials Science》索引2020年第14卷第3期,共10页

基　　金：This work was financially supported by the National Natural Science Foundation of China (Grant No. 21405105);the Shanghai Natural Science Foundation (14ZR1429300);the State Key Laboratory of Green Catalysis of Sichuan Institutes of Higher Education (LZJ1703). 摘　　要：Defect-rich hierarchical sponge-like TiO2 nanoparticles were successfully synthesized via the combined one-step hydrothermal method and chemical reduction approach.SEM and TEM images showed their porous structure densely packed with even smaller TiO2 particles,while photocatalytic results manifested their superior photocatalytic performance and high stability.The RhB solution(10 ppm)could be absolutely degraded in 60 min,and the degradation rate was twice that of the sample without the treatment by NaBH4.Besides,the TC solution(10 ppm)could be removed by 74.3%in 20 min.PEC measurements also displayed that the photoelectrode based on such defectrich TiO2 nanoparticles had small resistance and improved charge transfer rate.The improved performance can be assigned to rich defects and phase junctions,which was supported by characterization results.The presence of rich defects and phase junctions could not only promote the separation of photogenerated charge carriers,but also accelerate the electron transfer,beneficial for both the photocatalytic and the PEC performance.It is expected that the obtained hierarchical sponge-like TiO2 nanoparticles with rich defects have great potential for photocatalytic applications. 关键词：TiO2 hydrothermal method nanoparticles photocatalytic performance photoelectrochemical performance DEFECTS

相关文献

参考文献（44）
引证文献（1）
耦合文献（12）

参考文献(44)

引证文献(1)

耦合文献(12)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Synthesis of defect-rich hierarchical sponge-like TiO2 nanoparticles and their improved photocatalytic and photoelectrochemical performance

参考文献(44)

引证文献(1)

耦合文献(12)

用户提示