Effect of Particle Size on Mechanical Properties and Fracture Behaviors of Age-Hardening SiC/Al–Zn–Mg–Cu Composites

查看全文 作　　者：Guonan [1,2]Ma;Dong [1]Wang;Bolv [1]Xiao;Zongyi [1]Ma 高影响力作者 机构地区：[1]Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;[2]School of Materials Science and Engineering,University of Science and Technology of China,Shenyang 110016,China高影响力机构 出　　处：《Acta Metallurgica Sinica(English Letters)》索引2021年第34卷第10期,共13页高影响力期刊 基　　金：the National Key R&D Program of China(No.2017YFB0703104);the National Natural Science Foundation of China(Grant Nos.51771193 and 51931009)。 摘　　要：15 vol.% SiC/Al-6.5Zn-2.8 Mg-1.7 Cu(wt%) composites with varying particle sizes(3.5, 7.0, 14 and 20 μm), i.e., C-3.5, C-7.0, C-14, and C-20, respectively, were fabricated by powder metallurgy(PM) method and subjected to microstructural examination. The effect of particle size on mechanical properties and fracture behaviors of the T6-treated composites was revealed and analyzed in detail. Element distribution and precipitates variations in the composites with varying particle sizes were emphatically considered. Results indicated that both tensile strength and plasticity of the T6-treated composites increased first and then decreased with particle size decreasing. The C-7.0 composite simultaneously exhibited the highest ultimate tensile strength(UTS) of 686 MPa and best elongation(El.) of 3.1%. The smaller-sized SiC particle would introduce more oxide impurities, which would react with the alloying element in the matrix to cause Mg segregation and depletion. According to strengthening mechanism analysis, the weakening of precipitation strengthening in the T6-treated C-3.5 composite was the main cause of the lower tensile strength. Additionally, the larger SiC particle, the more likely to fracture, especially in the composites with high yield strength. For the T6-treated C-20 composites, more than 75% SiC particles were broken up, resulting in the lowest plasticity. As decreasing particle size, the fracture behaviors of the T6-treated composites would change from particle fracture to matrix alloy fracture gradually. 关 键 词：Metal matrix composites Mechanical properties Particle size Fracture behaviors Strengthening mechanisms
相关文献

参考文献(40)

引证文献(5)

耦合文献(14)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费