| 2 | Optimum Calcination Condition of Waste Stabilized Adobe for Alkali Activated High Volume Adobe-Slag Binder Cured at Room Temperature显示文摘This study aims to determine the most convenient calcination temperature and calcination duration of wastestabilized Adobe(AB)to produce a new alkali-activated binder.Waste-stabilized Adobe mainly consists of soil,CaCO3 as a stabilizer,and straw(for strengthening).The availability of raw materials for making Adobe presents the waste-stabilized Adobe as a potential product for a new alkali-activated binder.Waste-stabilized Adobe collected from an abandoned damaged building in the village of Inonu in Northern Cyprus,ground and calcined at the following temperatures:450,550,650,750,850,and 950℃.The calcination at each temperature was held for different durations 1,3,5,and 7 h.Raw and calcined waste stabilized Adobe structures were investigated using XRF,TGA-DTA,XRD,FTIR,and SEM.Considering technical and environmental views related to energy consumption,waste stabilized Adobe calcined at 750℃ for 1 h presented the most promising results regarding the production of a new precursor for alkali-activated binder.This study also presents the effect of ground granulated blast furnace slag(GGBFS)usage on the fresh and hardened properties of optimum calcined AB-based alkali-activated pastes cured at room temperature.GGBFS was used to partially replace AB to form a binary composite raw material system and seven experimental groups were designed according to replacement levels of 0%,5%,10%,15%,20%,25%and 30%(by mass).Alkali-activated high volume waste-stabilized Adobe-slag pastes prepared using Na2SiO3-to-NaOH ratio of 2 and 12 M concentration of Sodium Hydroxide.The fresh property as flowability and the hardened property as the compressive strength of the alkali-activated pastes with different GGBFS contents were investigated.The results indicated that the incorporation of GGBFS increased the flowability of fresh alkali-activated pastes.A 28-day compressive strength of 43.75 MPa can be obtained by a 30%replacement level of GGBFS. | Brya Aldawoodi Salaheddin Sabri Abdulmounem Alchekh Wis | 2022 | Journal of Renewable Materials2022，10，5： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员