| 1 | Microstructures and mechanical properties of a newly developed high-pressure die casting Mg-Zn-RE alloy显示文摘A newly developed Mg-4Zn-2La-3Y alloy with high strength was fabricated by high-pressure die casting method,and its microstructures were thoroughly studied using transmission electron microscopy.The results demonstrate that it owns fine grains and approximately highly interconnected intermetallic phase skeletons,and exhibits ultra-high strength at both room and high temperatures.Interestingly,the eutectic intermetallic skeleton of this alloys is consisted of numerous fine particles,which are mainly consisted of two intermetallic phases,namely W and Mg12RE.Multiple{101}twins and SFs were found in the Mg12RE phase while a few of SFs in the W phase.Additionally,minor long-period stacking ordered phase was observed in the eutectoid phase,and it probably nucleated on the Mg12RE phase following a certain OR as(0002)14H//(110)Mg12REand[1120]14H//[111]Mg12RE,or(0002)14H//(211)Mg12REand[1120]14H//[111]Mg12RE.This special intermetallic skeleton with many interfaces and planar faults can efficiently transfer dislocations across grain boundaries,and this is the key factor for the outstanding mechanical properties of the studied alloy. | Xiru Hua Qiang Yang Dongdong Zhang Fanzhi Meng Chong Chen Zihao You Jinghuai Zhang Shuhui Lv Jian Meng | 2020 | Journal of Materials Science & Technology2020，52，18： | 3 |
| 3 | Effect of Semi-solid Isothermal Heat Treatment on Microstructure of VW63Z Alloy显示文摘The effects of isothermal heat treatment on the semi-solid microstructure evolution of VW63Z(Mg-6Gd-3Y-0.4Zr,wt.%)alloy are studied.It shows that the microstructure of VW63Z alloy could transform from equiaxed crystal to semi-solid spherical crystal after isothermal heat treatment above 620℃.With the heating temperature elevating from 620℃ to 635℃ and the holding time prolonging from 10 min to 35 min,the liquid fraction increases gradually.The semi-solid microstructure evolution of VW63Z alloy can be divided into three stages,i.e.,particle coarsening and spheroidization;particle necking,coalescence,and Ostwald ripening;and dynamic equilibrium.The semi-solid process window of VW63Z alloy ranges from 620℃ to 635℃,where the best process parameters are holding at 635℃ for 20 min-30 min.The solid fraction,the average particle size,and the shape factor are 41.1%-53.8%,81.5μm-83.2μm,and 0.70-0.75,respectively.The maximum relative deviations of the solid fraction,the particle size,and the shape factor at different heights of the same billet are 44.6%,17.4%,and 16.6%,respectively,which means that it should pay attention to the uniformity of edge and core of VW63Z alloy during isothermal heat treatment.The driving force of microstructure is supposed to be the reduction of solid-liquid interface free energy. | GONG Zhengxuan PANG Song JI Song DONG Xiwang HOU Xiangwu CHEN Ge HUA Xiru WU Lili JIANG Shanyao XIAO Lü | 2022 | 上海航天(中英文)2022，39，1： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员