| 5 | Enhancing magnetic properties of anisotropic NdDyFeCoNbCuB powder by applying magnetic field at high temperature during hydrogen desorption显示文摘Anisotropic powder was prepared with precursor(NdDy)-(FeCoNbCu)-B sintered magnets by hydrogen decrepitation,desorption,and subsequent annealing treatment.The hydrogen desorption was performed in magnetic fields of 0,1,3,and 5 T.The orientation of tetragonal phase grains of the powder was evaluated from the hysteresis loops measured by extraction magnetometer.Residual hydrogen content of the powder was evaluated by thermal-magnetic analysis.The powder with Hcj,Br,and(BH)max of 1138 kA·m-1,1.029 T,and 172.5 kJ·m-3,respectively,was achieved under the condition of the magnetic field of 3 T.Magnetic properties of the powder,especially,the remanence of the powder,are enhanced upon magnetic fields,which is due to better orientation of powder particles and less residual hydrogen in the powder resulted from the magnetic field during the hydrogen desorption process. | LUO Jianjun P. De Rango D. Fruchart MEI Jinna HU Rui LI Jinshan ZHOU Lian | 2010 | Rare Metals2010，29，5： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员