2篇
您的检索式：作者名="QIAO ZhiXia"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | A new type-γ'/γ''coprecipitation behavior and its evolution mechanism in wrought Ni-based ATI 718Plus superalloy显示文摘In the precipitation-hardened Ni-based superalloy,typified by ATI 718 Plus,the nano-scaleγandγphase in duplet or triple coprecipitate morphology can provide superior high-temperature strength.Thus,it is of great sense to study the evolution ofγ’/γ’’coprecipitate during long term service at elevated temperature.In this study,the new-typeγ’/γ’’coprecipitates with a sandwich or compact configuration were found firstly in wrought ATI 718 Plus superalloy during long term thermal exposure at 705℃.These co-structure of theγ’/γ’’precipitates evidently inhibit the coarsening ofγ’phase.The increase of thermal exposure time evidently leads to the increase of the volume fraction ofγ’/γ’’coprecipitate and transformation of sandwich-typeγ’/γ’’coprecipitate to compact-typeγ’/γ’’coprecipitate,which is characterized asγphase precipitate at several faces of theγphase.The main evolution mechanism ofγ’/γ’’coprecipitates is element segregation,especially the composition variations of Al+Ti and Nb and their ratio of Al+Ti/Nb.In addition,the interfacial energy betweenγ’’phase andγmatrix also plays a key role on theγ’/γ’’coprecipitates evolution.The calculated results show that the longer thermal exposure time leads to the higher interfacial energy,which is beneficial for nucleation and precipitation ofγ’’phase on the faces ofγ’phase. | Qianying Guo Zongqing Ma Zhixia Qiao Chong Li Teng Zhang Jun Li Chenxi Liu Yongchang Liu | 2022 | Journal of Materials Science & Technology2022，，24： | 1 |
| 2 | Precipitates evolution and tensile behavior of wrought Ni-based ATI 718Plus superalloy during long-term thermal exposure显示文摘In this paper,the microstructure evolution and tensile behavior of wrought ATI 718 Plus superalloy during long-term thermal exposure(LTTE) were investigated.The γ’ phase evolves from spherical morphology to cuboidal morphology at 800℃,which is related to increasing γ’/γ misfit because of the increase of elastic energy.The amounts of η phase obviously increased and γ’ precipitate free zones(PFZs) were found in 800-LTTE samples due to the increase of η phase amount by consuming Al,Ti,and Nb.According to the formula of “MC+γ→M_(23)C_(6)+η”,η phase is also related to the decomposition of MC carbide,which involves the diffusion and segregation of Nb and Ti.In addition,some short rod-like and irregular Cr,Mo-rich σ phases were prone to precipitate near η phases after LTTE at 800℃ for 500 and 1000 h.σ phase has a crystallographic relationship with ηphase as(002)_(σ)//(10■0)_(η),[0■0]_(σ)//[01■0]_(η).The deteriorated tensile strength after LTTE is mainly attributed to that:(1) the evident coarsening of γ’ phase results in that the deformation mechanism transforms from stacking faults(SFs) shearing to Orowan looping,which is also convinced by calculated critical resolved shear stress(CRSS);(2) the noticeable increasing number of η phase contributes to stress concentration,resulting in micro-cracks formation;and (3) the apparently increasing number of η phase promotes the PFZs formation. | GUO QianYing JI KangKang ZHANG Teng QIAO ZhiXia LI Chong LI Jun LIU ChenXi LIU YongChang | 2022 | Science China(Technological Sciences)2022，65，6： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员