2篇
您的检索式：作者名="Xubing WEI"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Si-DLC films deposited by a novel method equipped with a co-potential auxiliary cathode for anti-corrosion and anti-wear application显示文摘A novel DLC film deposition method was proposed to realize the deposition of DLC film on the surface of complex shaped workpiece.Meanwhile,Si-DLC film was deposited on the surface of M2 high-speed steel(HSS M2)and 304 stainless steel(304SS),and the microstructure,surface roughness,mechanical properties,corrosion resistance and tribological properties of Si-DLC films were characterized in detail.Results show that Si-DLC film at different axial positions of the auxiliary cathode possesses similar microstructure,film thickness and surface roughness,and the as-deposited Si-DLC film shows the low intrinsic stress of<0.3 GPa.Compared with the 304SS substrate,the Si-DLC film presents more noble corrosion potential,lower corrosion current density and higher polarization resistance,exhibiting higher corrosion resistance.Moreover,the Si-DLC film exhibits higher hardness,elastic factor and plastic factor than HSS M2 substrate and the corresponding adhesive strength is more than 10 N.The Si-DLC film sliding against GCr15 steel ball shows a lower friction coefficient than that of HSS M2 substrate and the wear rate of GCr15 steel ball sliding against the Si-DLC is lower than that of HSS M2 substrate.In addition,this novel method was used to deposit Si-DLC film on gears,drills and bearings without rotating sample racks.As a consequence,this method possesses great potential and can be generalized for the deposition of DLC film on the surface of complex shape workpiece. | Xubing Wei Shaomiao Shi Chuangming Ning Zhibin Lu Guangan Zhang | 2022 | Journal of Materials Science & Technology2022，，14： | 4 |
| 2 | Friction reactions induced by selective hydrogenation of textured surface under lubricant conditions显示文摘The passivation of hydrogen atoms and the conformation of textured surfaces under oil-lubricated conditions are effective strategies to obtain amorphous carbon(a-C)films with extremely low friction.It is critical to understanding the influence mechanism of selective surface hydrogenation on the tribological behaviors of textured a-C film under oil-lubricated conditions.In particular,the interactions of hydrogen atoms and lubricants are confusing,which is enslaved to the in situ characterization technique.The reactive molecular dynamics(RMD)simulations were conducted to analyze the friction response of textured a-C films with selective hydrogenation surfaces under oil-lubricated conditions.The results indicate that the existence of hydrogen atoms on specific bump sites significantly decreases the friction coefficient(μ)of textured a-C film,which is highly dependent on the surface hydrogen content.The repulsion between hydrogen atoms and lubricant molecules prompts the formation of a dense lubricant film on the surface of the mating material.Interestingly,with the enhancement of the surface hydrogen content,the passivation of the friction interface and the repulsion between hydrogen atoms and lubricants play dominant roles in reducing the friction coefficient instead of hydrodynamic lubrication. | Naizhou DU Xubing WEI Xiaowei LI Zan CHEN Shiqi LU Jiaqing DING Cunao FENG Kai CHEN Jianghao QIAO Dekun ZHANG Kwang-Ryeol LEE Tiancai ZHANG | 2024 | Friction2024，12，1： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员